| Acrylonitrile Styrene (AS) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 1.07 to 1.08 | | Melt Mass Flow Rate (g/10 min) | 9.0 to 35 | | Flexural Modulus (psi) | 468000 to 541000 | | Tensile Strength (psi) | 9600 to 11000 | | Tensile Elongation (%) | 2.8 to 3.5 | | Rockwell Hardness | 127 | | Notched Izod Impact (ft·lb/in) | 0.244 to 0.341 | | DTUL at 66 psi (0.45 MPa) (°F) | -- | | DTUL at 264 psi (1.8 MPa) (°F) | 178 to 203 | | CLTE, Flow (in/in/°F) | 0.000033 |
SI
|
| Specific Gravity (g/cm³) | 1.07 to 1.08 | | Melt Mass Flow Rate (g/10 min) | 9.0 to 35 | | Flexural Modulus (MPa) | 3230 to 3730 | | Tensile Strength (MPa) | 66.2 to 76.1 | | Tensile Elongation (%) | 2.8 to 3.5 | | Rockwell Hardness | 127 | | Notched Izod Impact (J/m) | 13.0 to 18.2 | | DTUL at 66 psi (0.45 MPa) (°C) | -- | | DTUL at 264 psi (1.8 MPa) (°C) | 81.0 to 95.0 | | CLTE, Flow (cm/cm/°C) | 0.000060 |
|
|