| Acrylic (Acrylic) Typical Properties |
Share This Page
• Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.13 to 1.20 | 1.04 to 1.09 | 1.16 to 1.19 | 1.35 to 1.36 | | Melt Mass Flow Rate (g/10 min) | 0.30 to 4.7 | 0.40 to 9.1 | -- | 34 | | Flexural Modulus (psi) | 162000 to 523000 | 264000 to 493000 | 320000 to 478000 | 293000 to 372000 | | Tensile Strength (psi) | 5320 to 11700 | 725 to 9300 | 5620 to 10300 | 5780 to 6150 | | Tensile Elongation (%) | 0.0 to 7.3 | 2.0 to 59 | 2.7 to 250 | 55 to 170 | | Rockwell Hardness | 31 to 105 | 61 to 76 | 93 to 95 | 87 to 114 | | Notched Izod Impact (ft·lb/in) | 0.233 to 1.13 | 0.368 to 3.00 | 0.397 to 0.455 | 0.600 to 18.1 | | DTUL @ 66 psi (0.45 MPa) (°F) | 174 to 221 | 172 to 199 | 167 to 232 | 180 | | DTUL @ 264 psi (1.8 MPa) (°F) | 168 to 217 | 187 to 201 | 174 to 200 | 155 to 175 | | CLTE, Flow (in/in/°F) | 0.000030 to 0.000066 | -- | 0.000037 to 0.000045 | 0.000017 to 0.000045 |
SI
|
| Density (g/cm³) | 1.13 to 1.20 | 1.04 to 1.09 | 1.16 to 1.19 | 1.35 to 1.36 | | Melt Mass Flow Rate (g/10 min) | 0.30 to 4.7 | 0.40 to 9.1 | -- | 34 | | Flexural Modulus (MPa) | 1120 to 3610 | 1820 to 3400 | 2210 to 3290 | 2020 to 2560 | | Tensile Strength (MPa) | 36.7 to 80.8 | 5.00 to 64.2 | 38.8 to 70.9 | 39.8 to 42.4 | | Tensile Elongation (%) | 0.0 to 7.3 | 2.0 to 59 | 2.7 to 250 | 55 to 170 | | Rockwell Hardness | 31 to 105 | 61 to 76 | 93 to 95 | 87 to 114 | | Notched Izod Impact (J/m) | 12.4 to 60.2 | 19.6 to 160 | 21.2 to 24.3 | 32.0 to 964 | | DTUL @ 66 psi (0.45 MPa) (°C) | 78.9 to 105 | 77.8 to 92.8 | 75.0 to 111 | 82.2 | | DTUL @ 264 psi (1.8 MPa) (°C) | 75.6 to 103 | 86.2 to 94.1 | 79.2 to 93.1 | 68.3 to 79.3 | | CLTE, Flow (cm/cm/°C) | 0.000054 to 0.00012 | -- | 0.000067 to 0.000081 | 0.000030 to 0.000081 |
|
|