| Biodegradable Polymers (Biodeg Polymers) Typical Properties |
|
Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.19 to 1.35 | | Melt Mass Flow Rate (g/10 min) | 0.30 to 20 | | Flexural Modulus (psi) | 24300 to 526000 | | Tensile Strength (psi) | 1030 to 5820 | | Tensile Elongation (%) | 0.67 to 23 | | Rockwell Hardness | -- | | Notched Izod Impact (ft·lb/in) | 0.30 to 1.4 | | DTUL @ 66 psi (0.45 MPa) (°F) | 92.1 to 250 | | DTUL @ 264 psi (1.8 MPa) (°F) | 116 to 159 | | CLTE, Flow (in/in/°F) | -- |
SI
|
| Density (g/cm³) | 1.19 to 1.35 | | Melt Mass Flow Rate (g/10 min) | 0.30 to 20 | | Flexural Modulus (MPa) | 168 to 3630 | | Tensile Strength (MPa) | 7.13 to 40.1 | | Tensile Elongation (%) | 0.67 to 23 | | Rockwell Hardness | -- | | Notched Izod Impact (J/m) | 16 to 75 | | DTUL @ 66 psi (0.45 MPa) (°C) | 33.4 to 121 | | DTUL @ 264 psi (1.8 MPa) (°C) | 46.8 to 70.4 | | CLTE, Flow (cm/cm/°C) | -- |
|
|