| Diallyl Phthalate (DAP) Typical Properties |
|
Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.88 to 2.00 | | Melt Mass Flow Rate (g/10 min) | -- | | Flexural Modulus (psi) | 1.64E+6 to 1.92E+6 | | Tensile Strength (psi) | 4500 | | Tensile Elongation (%) | -- | | Rockwell Hardness | -- | | Notched Izod Impact (ft·lb/in) | 1.0 to 1.1 | | DTUL @ 66 psi (0.45 MPa) (°F) | -- | | DTUL @ 264 psi (1.8 MPa) (°F) | 500 to 536 | | CLTE, Flow (in/in/°F) | 0.000017 |
SI
|
| Density (g/cm³) | 1.88 to 2.00 | | Melt Mass Flow Rate (g/10 min) | -- | | Flexural Modulus (MPa) | 11300 to 13200 | | Tensile Strength (MPa) | 31.0 | | Tensile Elongation (%) | -- | | Rockwell Hardness | -- | | Notched Izod Impact (J/m) | 54 to 60 | | DTUL @ 66 psi (0.45 MPa) (°C) | -- | | DTUL @ 264 psi (1.8 MPa) (°C) | 260 to 280 | | CLTE, Flow (cm/cm/°C) | 0.000030 |
|
|