| Fluoropolymer (Fluoropolymer)
Processing Information |
|
|
English
|
| Specific Gravity | 1.70 to 1.74 | 2.14 to 2.15 | 1.80 to 1.90 | 1.38 to 1.63 | 1.05 to 2.80 | 2.08 to 2.13 | 2.14 to 2.15 | 2.01 to 2.15 | 1.49 to 2.20 | 1.76 to 1.79 | | Mold Shrinkage, Flow (in/in) | 0.018 | 0.0070 | 0.023 | -- | -- | -- | -- | -- | 0.027 to 0.030 | 0.022 to 0.025 | | Melt Mass Flow Rate (g/10 min) | 2.3 to 30 | 1.0 to 22 | 8.9 to 20 | -- | 5.0 to 38 | -- | -- | 2.3 to 2.5 | -- | -- | | Drying Temperature (°F) | -- | 250 | -- | -- | -- | -- | -- | -- | -- | 250 to 302 | | Drying Time (hr) | -- | 3.0 | -- | -- | -- | -- | -- | -- | -- | 1.0 to 2.0 | | Suggested Max Moisture (%) | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | | Suggested Max Regrind (%) | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | | Injection Pressure (psi) | -- | 5500 | -- | 1750 | 10900 | -- | 5500 | -- | -- | 12500 | | Rear Temperature (°F) | -- | -- | 400 to 409 | -- | 374 to 410 | -- | 615 | -- | -- | 383 to 423 | | Middle Temperature (°F) | -- | -- | 418 to 460 | -- | 410 to 446 | -- | 638 | -- | -- | 340 to 440 | | Front Temperature (°F) | -- | -- | 418 to 519 | -- | 464 to 500 | -- | 700 | -- | -- | 405 to 465 | | Nozzle Temperature (°F) | -- | -- | 465 to 518 | -- | 464 to 500 | -- | 700 | -- | -- | 399 to 480 | | Processing (Melt) Temp (°F) | 613 to 628 | 688 | 788 | -- | 581 to 582 | -- | 626 to 700 | -- | -- | 463 to 465 | | Mold Temperature (°F) | 275 | 200 | 140 to 482 | 425 | 298 to 302 | -- | 356 to 400 | -- | -- | 160 to 162 |
SI
|
| Specific Gravity (g/cm³) | 1.69 to 1.74 | 2.13 to 2.15 | 1.79 to 1.90 | 1.37 to 1.62 | 1.05 to 2.79 | 2.07 to 2.12 | 2.14 to 2.15 | 2.00 to 2.14 | 1.49 to 2.20 | 1.76 to 1.79 | | Mold Shrinkage, Flow (cm/cm) | 0.018 | 0.0070 | 0.023 | -- | -- | -- | -- | -- | 0.027 to 0.030 | 0.022 to 0.025 | | Melt Mass Flow Rate (g/10 min) | 2.3 to 30 | 1.0 to 22 | 8.9 to 20 | -- | 5.0 to 38 | -- | -- | 2.3 to 2.5 | -- | -- | | Drying Temperature (°C) | -- | 121 | -- | -- | -- | -- | -- | -- | -- | 121 to 150 | | Drying Time (hr) | -- | 3.0 | -- | -- | -- | -- | -- | -- | -- | 1.0 to 2.0 | | Suggested Max Moisture (%) | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | | Suggested Max Regrind (%) | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | | Injection Pressure (MPa) | -- | 37.9 | -- | 12.1 | 75.0 | -- | 37.9 | -- | -- | 86.2 | | Rear Temperature (°C) | -- | -- | 204 to 210 | -- | 190 to 210 | -- | 324 | -- | -- | 195 to 217 | | Middle Temperature (°C) | -- | -- | 214 to 238 | -- | 210 to 230 | -- | 336 | -- | -- | 171 to 227 | | Front Temperature (°C) | -- | -- | 214 to 271 | -- | 240 to 260 | -- | 371 | -- | -- | 207 to 241 | | Nozzle Temperature (°C) | -- | -- | 241 to 270 | -- | 240 to 260 | -- | 371 | -- | -- | 204 to 249 | | Processing (Melt) Temp (°C) | 323 to 331 | 364 | 420 | -- | 305 to 306 | -- | 330 to 371 | -- | -- | 240 | | Mold Temperature (°C) | 135 | 93.3 | 60.0 to 250 | 218 | 148 to 150 | -- | 180 to 204 | -- | -- | 71.0 to 71.9 |
|
|