| Ionomer (Ionomer) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 0.937 to 0.973 | | Melt Mass Flow Rate (g/10 min) | -- | | Flexural Modulus (psi) | 7700 to 156000 | | Tensile Strength (psi) | 1200 to 6550 | | Tensile Elongation (%) | 5.0 to 470 | | Rockwell Hardness | 95 | | Notched Izod Impact (ft·lb/in) | 4.86 to 16.3 | | DTUL at 66 psi (0.45 MPa) (°F) | 100 to 146 | | DTUL at 264 psi (1.8 MPa) (°F) | 118 | | CLTE, Flow (in/in/°F) | 6.1E-6 to 0.000089 |
SI
|
| Specific Gravity (g/cm³) | 0.935 to 0.971 | | Melt Mass Flow Rate (g/10 min) | -- | | Flexural Modulus (MPa) | 53.1 to 1070 | | Tensile Strength (MPa) | 8.27 to 45.2 | | Tensile Elongation (%) | 5.0 to 470 | | Rockwell Hardness | 95 | | Notched Izod Impact (J/m) | 259 to 872 | | DTUL at 66 psi (0.45 MPa) (°C) | 38.0 to 63.3 | | DTUL at 264 psi (1.8 MPa) (°C) | 48.0 | | CLTE, Flow (cm/cm/°C) | 0.000011 to 0.00016 |
|
|