| Liquid Crystal Polymer (LCP)
Processing Information |
|
|
English
|
| Specific Gravity | 1.38 to 1.88 | | Mold Shrinkage, Flow (in/in) | -0.000095 to 0.0040 | | Melt Mass Flow Rate (g/10 min) | 14 | | Drying Temperature (°F) | 299 to 356 | | Drying Time (hr) | 3.0 to 8.0 | | Suggested Max Moisture (%) | 0.0100 | | Suggested Max Regrind (%) | 20 to 30 | | Injection Pressure (psi) | 4350 to 17500 | | Rear Temperature (°F) | 518 to 658 | | Middle Temperature (°F) | 536 to 672 | | Front Temperature (°F) | 541 to 687 | | Nozzle Temperature (°F) | 572 to 691 | | Processing (Melt) Temp (°F) | 554 to 718 | | Mold Temperature (°F) | 172 to 275 |
SI
|
| Specific Gravity (g/cm³) | 1.38 to 1.87 | | Mold Shrinkage, Flow (cm/cm) | -0.000095 to 0.0040 | | Melt Mass Flow Rate (g/10 min) | 14 | | Drying Temperature (°C) | 148 to 180 | | Drying Time (hr) | 3.0 to 8.0 | | Suggested Max Moisture (%) | 0.0100 | | Suggested Max Regrind (%) | 20 to 30 | | Injection Pressure (MPa) | 30.0 to 121 | | Rear Temperature (°C) | 270 to 348 | | Middle Temperature (°C) | 280 to 356 | | Front Temperature (°C) | 283 to 364 | | Nozzle Temperature (°C) | 300 to 366 | | Processing (Melt) Temp (°C) | 290 to 381 | | Mold Temperature (°C) | 77.7 to 135 |
|
|