| Liquid Crystal Polymer (LCP) Typical Properties |
|
Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.38 to 2.70 | | Melt Mass Flow Rate (g/10 min) | -- | | Flexural Modulus (psi) | 986000 to 2.86E+6 | | Tensile Strength (psi) | 6500 to 26800 | | Tensile Elongation (%) | 0.40 to 3.5 | | Rockwell Hardness | 53 to 105 | | Notched Izod Impact (ft·lb/in) | 0.37 to 2.1 | | DTUL @ 66 psi (0.45 MPa) (°F) | 527 to 572 | | DTUL @ 264 psi (1.8 MPa) (°F) | 424 to 511 | | CLTE, Flow (in/in/°F) | 5.6E-7 to 9.2E-6 |
SI
|
| Density (g/cm³) | 1.38 to 2.70 | | Melt Mass Flow Rate (g/10 min) | -- | | Flexural Modulus (MPa) | 6800 to 19800 | | Tensile Strength (MPa) | 44.8 to 185 | | Tensile Elongation (%) | 0.40 to 3.5 | | Rockwell Hardness | 53 to 105 | | Notched Izod Impact (J/m) | 20 to 110 | | DTUL @ 66 psi (0.45 MPa) (°C) | 275 to 300 | | DTUL @ 264 psi (1.8 MPa) (°C) | 218 to 266 | | CLTE, Flow (cm/cm/°C) | 1.0E-6 to 0.000017 |
|
|