| Methyl Methacrylate (MM) Typical Properties |
Share This Page
• Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.08 to 1.10 | 1.07 to 1.10 | | Melt Mass Flow Rate (g/10 min) | 30 | 0.50 to 6.4 | | Flexural Modulus (psi) | 305000 to 352000 | 256000 to 441000 | | Tensile Strength (psi) | 5800 to 7250 | 5020 to 7400 | | Tensile Elongation (%) | 3.5 to 20 | 3.0 to 62 | | Rockwell Hardness | -- | 29 to 95 | | Notched Izod Impact (ft·lb/in) | 1.11 to 1.87 | 0.570 to 2.43 | | DTUL @ 66 psi (0.45 MPa) (°F) | 183 to 201 | 181 | | DTUL @ 264 psi (1.8 MPa) (°F) | 171 to 194 | 145 to 182 | | CLTE, Flow (in/in/°F) | 0.000053 to 0.000056 | 0.000050 |
SI
|
| Density (g/cm³) | 1.08 to 1.10 | 1.07 to 1.10 | | Melt Mass Flow Rate (g/10 min) | 30 | 0.50 to 6.4 | | Flexural Modulus (MPa) | 2100 to 2430 | 1770 to 3040 | | Tensile Strength (MPa) | 40.0 to 50.0 | 34.6 to 51.0 | | Tensile Elongation (%) | 3.5 to 20 | 3.0 to 62 | | Rockwell Hardness | -- | 29 to 95 | | Notched Izod Impact (J/m) | 59.0 to 100 | 30.4 to 129 | | DTUL @ 66 psi (0.45 MPa) (°C) | 84.0 to 94.0 | 82.8 to 83.0 | | DTUL @ 264 psi (1.8 MPa) (°C) | 77.0 to 90.0 | 63.0 to 83.4 | | CLTE, Flow (cm/cm/°C) | 0.000095 to 0.00010 | 0.000090 |
|
|