| Polyamide (Nylon)
Processing Information |
|
|
English
|
| Specific Gravity | -- | 1.03 to 1.05 | 0.980 to 1.23 | 1.01 to 1.02 | 1.17 to 1.20 | 0.922 to 1.17 | 1.03 to 1.14 | 1.01 to 1.18 | 1.12 | 1.16 to 1.18 | 1.06 to 1.08 | 1.07 to 1.17 | 1.01 to 1.35 | 0.994 to 1.23 | 1.14 | 1.10 to 1.16 | -- | 1.14 | 1.10 to 1.21 | 0.992 to 1.20 | 0.959 to 1.06 | 1.08 to 1.10 | 1.08 to 1.13 | -- | 1.10 to 1.16 | | Mold Shrinkage, Flow (in/in) | -- | 0.012 to 0.015 | 0.0047 to 0.019 | 0.0040 to 0.0085 | 0.0033 to 0.083 | 0.000100 to 0.044 | 0.0070 to 0.013 | 0.0030 to 0.022 | 0.0045 to 0.0046 | 0.0065 | 0.0079 to 0.010 | 0.0030 to 0.020 | 0.0010 to 0.060 | 0.00015 to 0.075 | 0.015 to 0.017 | 0.0098 to 0.016 | -- | 0.010 | 0.00040 to 0.0052 | 0.0013 to 0.022 | 0.013 to 0.021 | 0.0098 to 0.014 | 0.0080 to 0.012 | -- | 0.013 to 0.020 | | Melt Mass Flow Rate (g/10 min) | -- | -- | -- | 7.0 to 20 | -- | -- | -- | 6.0 to 7.0 | -- | -- | 6.0 to 7.0 | -- | -- | 10 | -- | -- | -- | -- | -- | 0.52 to 6.5 | 1.0 to 7.5 | 4.0 to 40 | 3.0 | -- | 20 to 310 | | Drying Temperature (°F) | -- | 175 to 176 | 175 to 212 | 179 to 230 | 193 to 219 | 173 to 180 | 160 | 176 | -- | -- | 176 to 178 | 175 to 180 | 170 to 180 | 165 to 196 | -- | 176 to 177 | -- | -- | 160 to 176 | 174 to 180 | 167 to 194 | 203 to 222 | 160 | -- | 175 to 275 | | Drying Time (hr) | -- | 3.9 to 12 | 3.0 to 10 | 3.5 to 4.1 | 4.0 to 12 | 1.9 to 5.1 | 5.0 | 8.0 | -- | -- | 3.0 to 3.5 | 2.0 to 4.0 | 2.9 to 4.1 | 2.8 to 5.3 | -- | 2.8 to 3.0 | -- | -- | 5.0 to 18 | 3.0 to 9.1 | 2.9 to 3.0 | 3.0 to 3.5 | 5.0 | -- | 4.0 to 6.1 | | Suggested Max Moisture (%) | -- | 0.10 | 0.020 to 0.50 | 0.030 to 0.10 | 0.050 to 0.053 | 0.095 to 0.20 | -- | 0.10 | -- | -- | 0.20 | 0.020 to 0.20 | 0.020 to 0.25 | 0.15 to 0.20 | -- | 0.099 to 0.20 | -- | -- | 0.10 | 0.020 to 0.20 | -- | 0.00050 | -- | -- | 0.045 to 0.15 | | Suggested Max Regrind (%) | -- | 20 | 20 | -- | 20 | 19 to 26 | -- | -- | -- | -- | -- | -- | 25 | 20 to 25 | -- | 20 | -- | -- | -- | -- | -- | 20 | -- | -- | -- | | Injection Pressure (psi) | -- | 12400 to 12500 | 12400 to 12700 | -- | 9430 to 12700 | 1000 to 16400 | -- | 5080 to 9430 | -- | -- | 900 | 1250 to 14000 | 14000 to 14300 | 12100 to 15000 | -- | 1160 to 7380 | -- | -- | -- | 6530 to 14200 | -- | -- | -- | -- | 14000 to 15000 | | Rear Temperature (°F) | -- | 390 to 480 | 425 to 465 | 356 to 410 | 572 to 573 | 438 to 512 | 430 | -- | -- | -- | 490 to 491 | 420 to 451 | 440 to 550 | 496 to 543 | -- | 470 to 521 | -- | -- | 410 to 500 | 534 to 539 | 380 to 391 | 535 | 430 | -- | 579 to 618 | | Middle Temperature (°F) | -- | 410 to 480 | 426 to 475 | 374 to 428 | 585 to 591 | 442 to 490 | 445 | -- | -- | -- | 508 to 509 | 430 to 471 | 445 to 525 | 515 to 556 | -- | 470 to 1110 | -- | -- | 430 to 500 | 506 to 558 | 400 to 410 | 540 | 445 | -- | 518 to 635 | | Front Temperature (°F) | -- | 430 to 480 | 425 to 484 | 383 to 437 | 590 to 596 | 443 to 513 | 465 | -- | -- | -- | 473 to 527 | 440 to 490 | 440 to 515 | 499 to 569 | -- | 490 to 530 | -- | -- | 440 to 500 | 508 to 573 | 430 to 440 | 545 | 465 | -- | 612 to 615 | | Nozzle Temperature (°F) | -- | 430 | 442 to 477 | 383 to 428 | 554 to 608 | 423 to 514 | 485 | -- | -- | -- | 473 | 480 to 490 | 450 to 555 | 498 to 557 | -- | 490 to 626 | -- | -- | 445 to 500 | 499 to 537 | 450 to 460 | 550 | 485 | -- | 518 to 653 | | Processing (Melt) Temp (°F) | -- | 493 | 452 to 527 | 390 to 455 | 590 to 595 | 360 to 597 | 480 | 419 to 595 | -- | 617 | 446 to 505 | 480 to 550 | 470 to 513 | 515 to 565 | -- | 503 to 537 | -- | -- | 435 to 518 | 507 to 620 | 446 to 474 | 491 to 554 | 480 | -- | 592 to 631 | | Mold Temperature (°F) | -- | 125 | 100 to 188 | 68.0 to 87.8 | 212 to 238 | 138 to 177 | 95.0 | 122 to 194 | -- | 176 | 131 to 158 | 125 to 190 | 157 to 176 | 147 to 191 | -- | 154 to 180 | -- | -- | 45.0 to 230 | 100 to 300 | 100 to 168 | 149 to 177 | 95.0 | -- | 172 to 320 |
SI
|
| Specific Gravity (g/cm³) | -- | 1.03 to 1.04 | 0.978 to 1.23 | 1.01 to 1.02 | 1.17 to 1.19 | 0.920 to 1.17 | 1.03 to 1.14 | 1.01 to 1.18 | 1.12 | 1.16 to 1.18 | 1.06 to 1.08 | 1.07 to 1.17 | 1.01 to 1.35 | 0.991 to 1.23 | 1.13 to 1.14 | 1.10 to 1.16 | -- | 1.14 | 1.10 to 1.21 | 0.990 to 1.20 | 0.957 to 1.05 | 1.08 to 1.10 | 1.07 to 1.13 | -- | 1.10 to 1.16 | | Mold Shrinkage, Flow (cm/cm) | -- | 0.012 to 0.015 | 0.0047 to 0.019 | 0.0040 to 0.0085 | 0.0033 to 0.083 | 0.000100 to 0.044 | 0.0070 to 0.013 | 0.0030 to 0.022 | 0.0045 to 0.0046 | 0.0065 | 0.0079 to 0.010 | 0.0030 to 0.020 | 0.0010 to 0.060 | 0.00015 to 0.075 | 0.015 to 0.017 | 0.0098 to 0.016 | -- | 0.010 | 0.00040 to 0.0052 | 0.0013 to 0.022 | 0.013 to 0.021 | 0.0098 to 0.014 | 0.0080 to 0.012 | -- | 0.013 to 0.020 | | Melt Mass Flow Rate (g/10 min) | -- | -- | -- | 7.0 to 20 | -- | -- | -- | 6.0 to 7.0 | -- | -- | 6.0 to 7.0 | -- | -- | 10 | -- | -- | -- | -- | -- | 0.52 to 6.5 | 1.0 to 7.5 | 4.0 to 40 | 3.0 | -- | 20 to 310 | | Drying Temperature (°C) | -- | 79.4 to 80.0 | 79.4 to 100 | 81.5 to 110 | 89.6 to 104 | 78.5 to 82.3 | 71.1 | 80.0 | -- | -- | 79.9 to 81.3 | 79.4 to 82.2 | 76.7 to 82.2 | 73.8 to 91.3 | -- | 80.0 to 80.4 | -- | -- | 71.1 to 80.0 | 78.7 to 82.5 | 75.0 to 90.0 | 95.0 to 106 | 71.1 | -- | 79.4 to 135 | | Drying Time (hr) | -- | 3.9 to 12 | 3.0 to 10 | 3.5 to 4.1 | 4.0 to 12 | 1.9 to 5.1 | 5.0 | 8.0 | -- | -- | 3.0 to 3.5 | 2.0 to 4.0 | 2.9 to 4.1 | 2.8 to 5.3 | -- | 2.8 to 3.0 | -- | -- | 5.0 to 18 | 3.0 to 9.1 | 2.9 to 3.0 | 3.0 to 3.5 | 5.0 | -- | 4.0 to 6.1 | | Suggested Max Moisture (%) | -- | 0.10 | 0.020 to 0.50 | 0.030 to 0.10 | 0.050 to 0.053 | 0.095 to 0.20 | -- | 0.10 | -- | -- | 0.20 | 0.020 to 0.20 | 0.020 to 0.25 | 0.15 to 0.20 | -- | 0.099 to 0.20 | -- | -- | 0.10 | 0.020 to 0.20 | -- | 0.00050 | -- | -- | 0.045 to 0.15 | | Suggested Max Regrind (%) | -- | 20 | 20 | -- | 20 | 19 to 26 | -- | -- | -- | -- | -- | -- | 25 | 20 to 25 | -- | 20 | -- | -- | -- | -- | -- | 20 | -- | -- | -- | | Injection Pressure (MPa) | -- | 85.3 to 86.2 | 85.7 to 87.5 | -- | 65.0 to 87.5 | 6.89 to 113 | -- | 35.0 to 65.0 | -- | -- | 6.21 | 8.62 to 96.5 | 96.3 to 98.7 | 83.7 to 104 | -- | 8.00 to 50.9 | -- | -- | -- | 45.0 to 98.1 | -- | -- | -- | -- | 96.5 to 103 | | Rear Temperature (°C) | -- | 199 to 249 | 218 to 241 | 180 to 210 | 300 to 301 | 226 to 266 | 221 | -- | -- | -- | 254 to 255 | 216 to 233 | 227 to 288 | 258 to 284 | -- | 243 to 272 | -- | -- | 210 to 260 | 279 to 282 | 193 to 200 | 279 | 221 | -- | 304 to 325 | | Middle Temperature (°C) | -- | 210 to 249 | 219 to 246 | 190 to 220 | 307 to 310 | 228 to 254 | 229 | -- | -- | -- | 264 to 265 | 221 to 244 | 229 to 274 | 268 to 291 | -- | 243 to 600 | -- | -- | 221 to 260 | 263 to 292 | 204 to 210 | 282 | 229 | -- | 270 to 335 | | Front Temperature (°C) | -- | 221 to 249 | 218 to 251 | 195 to 225 | 310 to 313 | 228 to 267 | 241 | -- | -- | -- | 245 to 275 | 227 to 254 | 227 to 268 | 259 to 299 | -- | 254 to 277 | -- | -- | 227 to 260 | 264 to 301 | 221 to 227 | 285 | 241 | -- | 322 to 324 | | Nozzle Temperature (°C) | -- | 221 | 228 to 247 | 195 to 220 | 290 to 320 | 217 to 268 | 252 | -- | -- | -- | 245 | 249 to 255 | 232 to 291 | 259 to 292 | -- | 254 to 330 | -- | -- | 229 to 260 | 259 to 280 | 232 to 238 | 288 | 252 | -- | 270 to 345 | | Processing (Melt) Temp (°C) | -- | 256 | 233 to 275 | 199 to 235 | 310 to 313 | 182 to 314 | 249 | 215 to 313 | -- | 325 | 230 to 263 | 249 to 288 | 243 to 267 | 268 to 296 | -- | 262 to 281 | -- | -- | 224 to 270 | 264 to 327 | 230 to 245 | 255 to 290 | 249 | -- | 311 to 333 | | Mold Temperature (°C) | -- | 51.6 to 51.7 | 38.0 to 86.5 | 20.0 to 31.0 | 99.8 to 114 | 58.7 to 80.3 | 35.0 | 50.0 to 90.0 | -- | 80.0 | 55.0 to 70.0 | 51.7 to 87.8 | 69.4 to 79.8 | 63.8 to 88.1 | -- | 68.0 to 82.0 | -- | -- | 7.22 to 110 | 37.8 to 149 | 37.8 to 75.8 | 65.0 to 80.6 | 35.0 | -- | 78.0 to 160 |
|
|