| Polyamide (Nylon) Typical Properties |
|
Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.02 to 1.09 | 0.960 to 1.21 | 1.00 to 1.02 | 1.17 to 1.79 | 1.09 to 1.62 | 1.03 to 1.14 | 1.03 to 1.46 | 1.16 to 1.44 | 1.06 to 1.08 | 1.06 to 1.15 | 1.02 to 1.35 | 1.07 to 1.22 | 1.13 to 1.14 | 1.09 to 1.38 | 1.28 to 1.85 | 1.18 to 1.78 | 1.14 | 1.10 to 1.46 | 1.01 to 1.21 | 0.957 to 1.06 | 1.08 to 1.27 | 1.07 to 1.13 | 1.35 to 1.80 | 1.10 to 1.66 | | Melt Mass Flow Rate (g/10 min) | -- | -- | 7.0 to 20 | -- | 4.0 to 20 | -- | 6.0 to 7.0 | -- | 6.0 to 34 | 16 | -- | -- | 10 | -- | -- | -- | -- | 2.0 | 0.52 to 6.5 | 1.1 to 7.5 | 4.0 to 40 | 3.0 | -- | 20 to 310 | | Flexural Modulus (psi) | 22000 to 228000 | 16000 to 255000 | 11600 to 250000 | 50800 to 1.69E+6 | 227000 to 453000 | 384000 to 439000 | 29000 to 400000 | 421000 to 1.06E+6 | 227000 to 424000 | 263000 to 302000 | 43500 to 1.23E+6 | 218000 to 544000 | 290000 to 452000 | 255000 to 1.23E+6 | -- | -- | 435000 | 306000 to 1.51E+6 | 114000 to 1.40E+6 | 126000 to 319000 | 277000 to 345000 | 63500 to 68100 | 1.19E+6 to 3.49E+6 | 190000 to 2.07E+6 | | Tensile Strength (psi) | 4340 to 10300 | 3590 to 8540 | 1160 to 8750 | 4350 to 31100 | 5340 to 14200 | 10800 to 12300 | 3130 to 16900 | 13700 to 40600 | 4790 to 8060 | 6830 to 9500 | 3760 to 25100 | 6130 to 13200 | 7250 to 12900 | 7560 to 27700 | 21000 to 42400 | 12300 to 37800 | 13100 | 11100 to 26100 | 2850 to 16800 | 3190 to 7400 | 6350 to 9950 | 7500 to 8420 | 16000 to 41600 | 8040 to 38100 | | Tensile Elongation (%) | 2.0 to 56 | 0.60 to 200 | 19 to 400 | 0.56 to 53 | 0.40 to 25 | 10 to 84 | 190 to 200 | 1.9 to 12 | 3.0 to 51 | 2.4 to 100 | 2.0 to 32 | 0.70 to 19 | 19 to 180 | 1.5 to 18 | 1.9 to 3.1 | 1.5 to 9.0 | 15 | 2.5 to 15 | 1.5 to 53 | 5.0 to 88 | 7.0 to 100 | 300 to 500 | 0.60 to 2.7 | 1.0 to 5.7 | | Rockwell Hardness | 77 to 109 | 79 to 115 | -- | 90 to 100 | 110 to 123 | -- | 74 to 120 | -- | 105 | 112 to 116 | 113 to 118 | 79 to 122 | -- | 112 to 120 | -- | -- | 118 | -- | 110 to 121 | -- | 110 to 115 | -- | 120 to 121 | 108 to 125 | | Notched Izod Impact (ft·lb/in) | 0.30 to 2.1 | 0.30 to 3.0 | 3.2 | 0.75 to 1.9 | 0.19 to 1.8 | 0.70 to 1.5 | 0.80 to 20 | -- | 0.18 to 14 | 0.65 to 0.94 | 0.54 to 1.7 | 0.19 to 1.8 | 0.70 to 1.3 | 0.47 to 1.3 | -- | -- | 0.37 | 1.0 to 2.2 | 0.19 to 1.5 | 2.0 to 15 | 0.75 to 4.0 | 1.6 to 16 | 1.2 to 3.2 | 0.28 to 2.7 | | DTUL @ 66 psi (0.45 MPa) (°F) | 289 to 356 | 173 to 353 | 124 to 230 | 552 to 556 | 301 to 435 | 140 to 410 | 153 to 446 | 248 to 536 | 190 to 392 | 301 to 358 | 269 to 428 | 368 to 504 | 266 to 473 | 344 to 460 | -- | 239 to 491 | -- | 397 to 419 | 140 to 505 | 140 to 383 | 273 to 374 | -- | 453 to 461 | 523 to 608 | | DTUL @ 264 psi (1.8 MPa) (°F) | 103 to 351 | 111 to 332 | -- | 311 to 555 | 112 to 419 | 122 to 374 | 136 to 424 | 212 to 519 | 122 to 305 | 129 to 155 | 123 to 404 | 133 to 493 | 149 to 437 | 139 to 456 | 446 to 482 | 523 to 561 | 275 | 345 to 392 | 124 to 431 | 128 to 133 | 239 to 294 | -- | 417 to 457 | 220 to 572 | | CLTE, Flow (in/in/°F) | 0.000047 to 0.000062 | 5.6E-6 to 0.000095 | 0.000089 to 0.00013 | 9.2E-6 to 0.000047 | 1.7E-6 to 0.000063 | 0.000011 to 0.000094 | 0.000013 to 0.000050 | 8.3E-6 to 0.000014 | 0.000022 to 0.00016 | 0.000014 to 0.00011 | 7.8E-6 to 0.000068 | 8.3E-7 to 0.000056 | 9.4E-6 to 0.000036 | 7.4E-6 to 0.000045 | 5.6E-6 to 8.5E-6 | 8.3E-6 to 0.000011 | -- | 0.000011 to 0.000022 | 5.6E-6 to 0.000075 | 0.000022 | 0.000044 to 0.000051 | -- | 5.3E-6 to 0.000028 | 7.1E-6 to 0.000015 |
SI
|
| Density (g/cm³) | 1.02 to 1.09 | 0.960 to 1.21 | 1.00 to 1.02 | 1.17 to 1.79 | 1.09 to 1.62 | 1.03 to 1.14 | 1.03 to 1.46 | 1.16 to 1.44 | 1.06 to 1.08 | 1.06 to 1.15 | 1.02 to 1.35 | 1.07 to 1.22 | 1.13 to 1.14 | 1.09 to 1.38 | 1.28 to 1.85 | 1.18 to 1.78 | 1.14 | 1.10 to 1.46 | 1.01 to 1.21 | 0.957 to 1.06 | 1.08 to 1.27 | 1.07 to 1.13 | 1.35 to 1.80 | 1.10 to 1.66 | | Melt Mass Flow Rate (g/10 min) | -- | -- | 7.0 to 20 | -- | 4.0 to 20 | -- | 6.0 to 7.0 | -- | 6.0 to 34 | 16 | -- | -- | 10 | -- | -- | -- | -- | 2.0 | 0.52 to 6.5 | 1.1 to 7.5 | 4.0 to 40 | 3.0 | -- | 20 to 310 | | Flexural Modulus (MPa) | 152 to 1570 | 110 to 1760 | 80.0 to 1720 | 350 to 11600 | 1560 to 3130 | 2650 to 3030 | 200 to 2760 | 2900 to 7300 | 1570 to 2920 | 1820 to 2080 | 300 to 8490 | 1500 to 3750 | 2000 to 3110 | 1760 to 8460 | -- | -- | 3000 | 2110 to 10400 | 787 to 9660 | 869 to 2200 | 1910 to 2380 | 438 to 469 | 8230 to 24100 | 1310 to 14200 | | Tensile Strength (MPa) | 29.9 to 70.7 | 24.8 to 58.9 | 8.00 to 60.3 | 30.0 to 214 | 36.8 to 97.7 | 74.6 to 84.8 | 21.6 to 117 | 94.4 to 280 | 33.0 to 55.6 | 47.1 to 65.5 | 26.0 to 173 | 42.2 to 91.2 | 50.0 to 88.6 | 52.1 to 191 | 145 to 292 | 85.0 to 261 | 90.0 | 76.7 to 180 | 19.6 to 116 | 22.0 to 51.0 | 43.8 to 68.6 | 51.7 to 58.1 | 110 to 287 | 55.4 to 263 | | Tensile Elongation (%) | 2.0 to 56 | 0.60 to 200 | 19 to 400 | 0.56 to 53 | 0.40 to 25 | 10 to 84 | 190 to 200 | 1.9 to 12 | 3.0 to 51 | 2.4 to 100 | 2.0 to 32 | 0.70 to 19 | 19 to 180 | 1.5 to 18 | 1.9 to 3.1 | 1.5 to 9.0 | 15 | 2.5 to 15 | 1.5 to 53 | 5.0 to 88 | 7.0 to 100 | 300 to 500 | 0.60 to 2.7 | 1.0 to 5.7 | | Rockwell Hardness | 77 to 109 | 79 to 115 | -- | 90 to 100 | 110 to 123 | -- | 74 to 120 | -- | 105 | 112 to 116 | 113 to 118 | 79 to 122 | -- | 112 to 120 | -- | -- | 118 | -- | 110 to 121 | -- | 110 to 115 | -- | 120 to 121 | 108 to 125 | | Notched Izod Impact (J/m) | 16 to 110 | 16 to 160 | 170 | 40 to 100 | 10 to 98 | 37 to 78 | 43 to 1100 | -- | 9.7 to 750 | 35 to 50 | 29 to 89 | 10 to 95 | 37 to 69 | 25 to 68 | -- | -- | 20 | 53 to 120 | 10 to 81 | 110 to 800 | 40 to 210 | 85 to 860 | 65 to 170 | 15 to 150 | | DTUL @ 66 psi (0.45 MPa) (°C) | 143 to 180 | 78.4 to 179 | 51.0 to 110 | 289 to 291 | 149 to 224 | 60.0 to 210 | 67.0 to 230 | 120 to 280 | 88.0 to 200 | 150 to 181 | 132 to 220 | 187 to 262 | 130 to 245 | 174 to 238 | -- | 115 to 255 | -- | 203 to 215 | 60.0 to 263 | 60.0 to 195 | 134 to 190 | -- | 234 to 238 | 273 to 320 | | DTUL @ 264 psi (1.8 MPa) (°C) | 39.2 to 177 | 43.6 to 167 | -- | 155 to 291 | 44.3 to 215 | 50.0 to 190 | 58.0 to 218 | 100 to 271 | 50.0 to 152 | 53.6 to 68.1 | 50.7 to 207 | 55.9 to 256 | 65.0 to 225 | 59.6 to 236 | 230 to 250 | 273 to 294 | 135 | 174 to 200 | 51.3 to 222 | 53.3 to 56.0 | 115 to 145 | -- | 214 to 236 | 105 to 300 | | CLTE, Flow (cm/cm/°C) | 0.000084 to 0.00011 | 0.000010 to 0.00017 | 0.00016 to 0.00023 | 0.000017 to 0.000085 | 3.0E-6 to 0.00011 | 0.000019 to 0.00017 | 0.000024 to 0.000090 | 0.000015 to 0.000026 | 0.000040 to 0.00029 | 0.000025 to 0.00020 | 0.000014 to 0.00012 | 1.5E-6 to 0.00010 | 0.000017 to 0.000065 | 0.000013 to 0.000081 | 0.000010 to 0.000015 | 0.000015 to 0.000021 | -- | 0.000020 to 0.000040 | 0.000010 to 0.00014 | 0.000040 | 0.000079 to 0.000091 | -- | 9.5E-6 to 0.000051 | 0.000013 to 0.000026 |
|
|