| Polycaprolactone (PCL) Typical Properties |
|
Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.11 to 1.22 | | Melt Mass Flow Rate (g/10 min) | 3.0 to 40 | | Flexural Modulus (psi) | -- | | Tensile Strength (psi) | 750 to 4000 | | Tensile Elongation (%) | 650 to 800 | | Rockwell Hardness | -- | | Notched Izod Impact (ft·lb/in) | -- | | DTUL @ 66 psi (0.45 MPa) (°F) | -- | | DTUL @ 264 psi (1.8 MPa) (°F) | -- | | CLTE, Flow (in/in/°F) | -- |
SI
|
| Density (g/cm³) | 1.11 to 1.22 | | Melt Mass Flow Rate (g/10 min) | 3.0 to 40 | | Flexural Modulus (MPa) | -- | | Tensile Strength (MPa) | 5.17 to 27.6 | | Tensile Elongation (%) | 650 to 800 | | Rockwell Hardness | -- | | Notched Izod Impact (J/m) | -- | | DTUL @ 66 psi (0.45 MPa) (°C) | -- | | DTUL @ 264 psi (1.8 MPa) (°C) | -- | | CLTE, Flow (cm/cm/°C) | -- |
|
|