| Polyketone (PK) Typical Properties |
|
Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.23 to 1.45 | | Melt Mass Flow Rate (g/10 min) | 5.8 to 7.3 | | Flexural Modulus (psi) | 220000 to 330000 | | Tensile Strength (psi) | 5500 to 8740 | | Tensile Elongation (%) | 20 to 310 | | Rockwell Hardness | 105 | | Notched Izod Impact (ft·lb/in) | 0.90 to 4.6 | | DTUL @ 66 psi (0.45 MPa) (°F) | 398 to 410 | | DTUL @ 264 psi (1.8 MPa) (°F) | 220 to 221 | | CLTE, Flow (in/in/°F) | 0.000056 |
SI
|
| Density (g/cm³) | 1.23 to 1.45 | | Melt Mass Flow Rate (g/10 min) | 5.8 to 7.3 | | Flexural Modulus (MPa) | 1520 to 2280 | | Tensile Strength (MPa) | 37.9 to 60.3 | | Tensile Elongation (%) | 20 to 310 | | Rockwell Hardness | 105 | | Notched Izod Impact (J/m) | 48 to 250 | | DTUL @ 66 psi (0.45 MPa) (°C) | 203 to 210 | | DTUL @ 264 psi (1.8 MPa) (°C) | 104 to 105 | | CLTE, Flow (cm/cm/°C) | 0.00010 |
|
|