| Polylactic Acid (PLA)
Processing Information |
|
|
English
|
| Specific Gravity | 1.24 to 1.31 | | Mold Shrinkage, Flow (in/in) | 0.0040 | | Melt Mass Flow Rate (g/10 min) | 5.6 to 20 | | Drying Temperature (°F) | 122 to 212 | | Drying Time (hr) | 4.0 | | Suggested Max Moisture (%) | 0.025 to 0.032 | | Suggested Max Regrind (%) | -- | | Injection Pressure (psi) | -- | | Rear Temperature (°F) | 311 to 355 | | Middle Temperature (°F) | 338 to 410 | | Front Temperature (°F) | 356 to 420 | | Nozzle Temperature (°F) | 338 to 420 | | Processing (Melt) Temp (°F) | 338 to 410 | | Mold Temperature (°F) | 75.0 to 85.0 |
SI
|
| Specific Gravity (g/cm³) | 1.23 to 1.31 | | Mold Shrinkage, Flow (cm/cm) | 0.0040 | | Melt Mass Flow Rate (g/10 min) | 5.6 to 20 | | Drying Temperature (°C) | 50.0 to 100 | | Drying Time (hr) | 4.0 | | Suggested Max Moisture (%) | 0.025 to 0.032 | | Suggested Max Regrind (%) | -- | | Injection Pressure (MPa) | -- | | Rear Temperature (°C) | 155 to 179 | | Middle Temperature (°C) | 170 to 210 | | Front Temperature (°C) | 180 to 216 | | Nozzle Temperature (°C) | 170 to 216 | | Processing (Melt) Temp (°C) | 170 to 210 | | Mold Temperature (°C) | 23.9 to 29.4 |
|
|