| Polylactic Acid (PLA) Typical Properties |
Share This Page
• Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.23 to 1.25 | | Melt Mass Flow Rate (g/10 min) | 0.20 to 24 | | Flexural Modulus (psi) | 319000 to 1.38E+6 | | Tensile Strength (psi) | 2360 to 10000 | | Tensile Elongation (%) | 1.0 to 8.7 | | Rockwell Hardness | 84 to 115 | | Notched Izod Impact (ft·lb/in) | 0.223 to 0.620 | | DTUL @ 66 psi (0.45 MPa) (°F) | 115 to 252 | | DTUL @ 264 psi (1.8 MPa) (°F) | 118 to 131 | | CLTE, Flow (in/in/°F) | -- |
SI
|
| Density (g/cm³) | 1.23 to 1.25 | | Melt Mass Flow Rate (g/10 min) | 0.20 to 24 | | Flexural Modulus (MPa) | 2200 to 9500 | | Tensile Strength (MPa) | 16.3 to 69.0 | | Tensile Elongation (%) | 1.0 to 8.7 | | Rockwell Hardness | 84 to 115 | | Notched Izod Impact (J/m) | 11.9 to 33.1 | | DTUL @ 66 psi (0.45 MPa) (°C) | 46.3 to 122 | | DTUL @ 264 psi (1.8 MPa) (°C) | 48.0 to 55.0 | | CLTE, Flow (cm/cm/°C) | -- |
|
|