| Polymethylpentene (PMP) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 0.833 to 0.910 | 0.835 to 0.841 | | Melt Mass Flow Rate (g/10 min) | 5.0 to 70 | 18 to 26 | | Flexural Modulus (psi) | 69800 to 278000 | 91400 to 257000 | | Tensile Strength (psi) | 1660 to 6700 | 2890 to 4400 | | Tensile Elongation (%) | 10 to 440 | 11 to 60 | | Rockwell Hardness | -- | 42 to 92 | | Notched Izod Impact (ft·lb/in) | 0.987 to 1.02 | 0.351 to 0.525 | | DTUL at 66 psi (0.45 MPa) (°F) | 185 to 212 | 167 to 262 | | DTUL at 264 psi (1.8 MPa) (°F) | 120 to 132 | -- | | CLTE, Flow (in/in/°F) | -- | 0.000065 to 0.00021 |
SI
|
| Specific Gravity (g/cm³) | 0.831 to 0.908 | 0.833 to 0.839 | | Melt Mass Flow Rate (g/10 min) | 5.0 to 70 | 18 to 26 | | Flexural Modulus (MPa) | 481 to 1920 | 630 to 1770 | | Tensile Strength (MPa) | 11.4 to 46.2 | 19.9 to 30.4 | | Tensile Elongation (%) | 10 to 440 | 11 to 60 | | Rockwell Hardness | -- | 42 to 92 | | Notched Izod Impact (J/m) | 52.7 to 54.4 | 18.8 to 28.0 | | DTUL at 66 psi (0.45 MPa) (°C) | 85.0 to 100 | 75.0 to 128 | | DTUL at 264 psi (1.8 MPa) (°C) | 48.9 to 55.3 | -- | | CLTE, Flow (cm/cm/°C) | -- | 0.00012 to 0.00038 |
|
|