| Polyphenylene Ether (PPE) Typical Properties |
|
Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.05 to 1.09 | 1.04 to 1.12 | 1.07 to 1.25 | 0.968 to 1.08 | 0.928 to 1.10 | | Melt Mass Flow Rate (g/10 min) | 0.10 to 55 | 1.3 to 44 | 6.3 to 27 | 4.4 to 16 | 4.7 to 33 | | Flexural Modulus (psi) | 298000 to 387000 | 293000 to 444000 | 255000 to 400000 | 117000 to 512000 | 3190 to 58900 | | Tensile Strength (psi) | 5040 to 10200 | 5630 to 10800 | 6260 to 9660 | 4000 to 8700 | 1860 to 3950 | | Tensile Elongation (%) | 1.8 to 61 | 0.88 to 53 | 2.1 to 51 | 2.6 to 12 | 85 to 400 | | Rockwell Hardness | 118 to 122 | 113 to 124 | 110 to 119 | -- | -- | | Notched Izod Impact (ft·lb/in) | 0.40 to 7.1 | 0.33 to 5.7 | 0.60 to 5.5 | 0.016 to 11 | -- | | DTUL @ 66 psi (0.45 MPa) (°F) | 200 to 340 | 190 to 325 | 306 to 385 | 228 to 302 | 185 | | DTUL @ 264 psi (1.8 MPa) (°F) | 169 to 339 | 162 to 305 | 158 to 379 | 160 to 282 | -- | | CLTE, Flow (in/in/°F) | 0.000033 to 0.000040 | 0.000031 to 0.000051 | 0.000043 to 0.000056 | 0.000027 to 0.000090 | -- |
SI
|
| Density (g/cm³) | 1.05 to 1.09 | 1.04 to 1.12 | 1.07 to 1.25 | 0.968 to 1.08 | 0.928 to 1.10 | | Melt Mass Flow Rate (g/10 min) | 0.10 to 55 | 1.3 to 44 | 6.3 to 27 | 4.4 to 16 | 4.7 to 33 | | Flexural Modulus (MPa) | 2050 to 2670 | 2020 to 3060 | 1760 to 2760 | 810 to 3530 | 22.0 to 406 | | Tensile Strength (MPa) | 34.8 to 70.5 | 38.8 to 74.4 | 43.1 to 66.6 | 27.6 to 60.0 | 12.8 to 27.2 | | Tensile Elongation (%) | 1.8 to 61 | 0.88 to 53 | 2.1 to 51 | 2.6 to 12 | 85 to 400 | | Rockwell Hardness | 118 to 122 | 113 to 124 | 110 to 119 | -- | -- | | Notched Izod Impact (J/m) | 21 to 380 | 18 to 300 | 32 to 300 | 0.85 to 590 | -- | | DTUL @ 66 psi (0.45 MPa) (°C) | 93.3 to 171 | 87.6 to 163 | 152 to 196 | 109 to 150 | 85.0 | | DTUL @ 264 psi (1.8 MPa) (°C) | 76.0 to 170 | 72.0 to 152 | 70.0 to 193 | 71.1 to 139 | -- | | CLTE, Flow (cm/cm/°C) | 0.000059 to 0.000072 | 0.000056 to 0.000092 | 0.000078 to 0.00010 | 0.000049 to 0.00016 | -- |
|
|