| Polyphenylene Sulfide (PPS) Typical Properties |
Share This Page
• Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.26 to 1.75 | 1.15 to 1.31 | -- | 1.45 to 1.61 | 1.44 to 1.59 | | Melt Mass Flow Rate (g/10 min) | 75 to 5000 | -- | -- | -- | -- | | Flexural Modulus (psi) | 300000 to 2.05E+6 | 145000 to 377000 | -- | 377000 to 435000 | 1.22E+6 to 1.56E+6 | | Tensile Strength (psi) | 4190 to 25500 | 3950 to 8370 | -- | 5500 to 8560 | 16400 to 18600 | | Tensile Elongation (%) | 0.16 to 5.0 | 0.50 to 100 | -- | 3.0 to 4.6 | 7.0 to 10 | | Rockwell Hardness | 92 to 126 | -- | -- | -- | -- | | Notched Izod Impact (ft·lb/in) | 0.100 to 3.08 | 0.800 to 1.66 | -- | 0.600 to 0.611 | 1.09 to 1.65 | | DTUL @ 66 psi (0.45 MPa) (°F) | 395 to 536 | 210 to 266 | -- | 264 to 354 | 491 to 495 | | DTUL @ 264 psi (1.8 MPa) (°F) | 204 to 518 | 175 to 451 | -- | 212 to 277 | 513 | | CLTE, Flow (in/in/°F) | 8.5E-6 to 0.000031 | 0.000036 to 0.00015 | -- | 0.000029 | 0.000021 to 0.000022 |
SI
|
| Density (g/cm³) | 1.26 to 1.75 | 1.15 to 1.31 | -- | 1.45 to 1.61 | 1.44 to 1.59 | | Melt Mass Flow Rate (g/10 min) | 75 to 5000 | -- | -- | -- | -- | | Flexural Modulus (MPa) | 2070 to 14100 | 1000 to 2600 | -- | 2600 to 3000 | 8430 to 10800 | | Tensile Strength (MPa) | 28.9 to 176 | 27.3 to 57.7 | -- | 37.9 to 59.0 | 113 to 128 | | Tensile Elongation (%) | 0.16 to 5.0 | 0.50 to 100 | -- | 3.0 to 4.6 | 7.0 to 10 | | Rockwell Hardness | 92 to 126 | -- | -- | -- | -- | | Notched Izod Impact (J/m) | 5.34 to 164 | 42.7 to 88.3 | -- | 32.0 to 32.6 | 58.0 to 88.0 | | DTUL @ 66 psi (0.45 MPa) (°C) | 201 to 280 | 98.9 to 130 | -- | 129 to 179 | 255 to 257 | | DTUL @ 264 psi (1.8 MPa) (°C) | 95.8 to 270 | 79.4 to 233 | -- | 99.9 to 136 | 267 | | CLTE, Flow (cm/cm/°C) | 0.000015 to 0.000055 | 0.000066 to 0.00027 | -- | 0.000052 | 0.000038 to 0.000040 |
|
|