| Polysulfone (PSU) Typical Properties |
|
Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.37 | 1.35 to 1.38 | 1.28 to 1.35 | 1.22 to 1.24 | | Melt Mass Flow Rate (g/10 min) | -- | 20 to 76 | 16 to 45 | 4.0 to 7.2 | | Flexural Modulus (psi) | 398000 to 400000 | 357000 to 424000 | 285000 to 405000 | 290000 to 407000 | | Tensile Strength (psi) | 8500 to 13000 | 11800 to 13200 | 8880 to 11000 | 7920 to 11000 | | Tensile Elongation (%) | 6.5 to 10 | 5.0 to 7.2 | 6.9 to 90 | 3.7 to 77 | | Rockwell Hardness | 120 | 120 | 80 to 120 | 119 to 120 | | Notched Izod Impact (ft·lb/in) | 1.2 to 1.6 | 0.50 to 1.8 | 2.4 to 13 | 0.94 to 1.4 | | DTUL @ 66 psi (0.45 MPa) (°F) | 405 | 405 to 424 | 417 to 428 | 351 to 358 | | DTUL @ 264 psi (1.8 MPa) (°F) | 400 | 382 to 406 | 384 to 410 | 328 to 352 | | CLTE, Flow (in/in/°F) | 0.000031 | 0.000026 to 0.000039 | 0.000030 to 0.000031 | 0.000029 to 0.000034 |
SI
|
| Density (g/cm³) | 1.37 | 1.35 to 1.38 | 1.28 to 1.35 | 1.22 to 1.24 | | Melt Mass Flow Rate (g/10 min) | -- | 20 to 76 | 16 to 45 | 4.0 to 7.2 | | Flexural Modulus (MPa) | 2740 to 2760 | 2460 to 2920 | 1960 to 2790 | 2000 to 2810 | | Tensile Strength (MPa) | 58.6 to 89.6 | 81.6 to 91.0 | 61.3 to 76.1 | 54.6 to 75.9 | | Tensile Elongation (%) | 6.5 to 10 | 5.0 to 7.2 | 6.9 to 90 | 3.7 to 77 | | Rockwell Hardness | 120 | 120 | 80 to 120 | 119 to 120 | | Notched Izod Impact (J/m) | 64 to 85 | 27 to 93 | 130 to 690 | 50 to 73 | | DTUL @ 66 psi (0.45 MPa) (°C) | 207 | 207 to 218 | 214 to 220 | 177 to 181 | | DTUL @ 264 psi (1.8 MPa) (°C) | 204 | 194 to 208 | 195 to 210 | 164 to 178 | | CLTE, Flow (cm/cm/°C) | 0.000056 | 0.000047 to 0.000071 | 0.000054 to 0.000056 | 0.000052 to 0.000062 |
|
|