| Polyurethane (PUR) Typical Properties |
Share This Page
• Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 0.830 to 1.38 | 1.13 | 1.04 to 1.21 | 1.15 to 1.23 | 1.25 to 1.52 | 1.20 to 1.25 | 1.16 to 1.27 | 1.02 to 1.07 | 1.06 to 1.43 | 0.998 to 1.13 | 1.04 to 1.21 | 0.239 to 1.25 | 1.01 to 1.21 | | Melt Mass Flow Rate (g/10 min) | 3.0 to 20 | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | | Flexural Modulus (psi) | 5500 to 390000 | -- | -- | -- | 376000 to 445000 | -- | -- | 1040 to 100000 | -- | -- | 81000 to 116000 | 15000 to 309000 | -- | | Tensile Strength (psi) | 11.0 to 9010 | 3600 to 7200 | 250 to 3400 | 2470 to 8600 | 5630 to 13600 | 1790 to 7640 | 5270 to 9000 | 3000 to 6750 | 171 to 7050 | 142 to 7600 | 2000 to 9000 | 560 to 7500 | 924 to 3580 | | Tensile Elongation (%) | 2.0 to 54 | 310 to 530 | 75 to 630 | 220 to 890 | 6.8 to 650 | 390 to 700 | 280 to 710 | 180 to 850 | 500 to 750 | 190 to 580 | 180 to 570 | 4.2 to 18 | 130 to 710 | | Rockwell Hardness | 111 | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | | Notched Izod Impact (ft·lb/in) | 0.0100 to 1.61 | -- | -- | -- | 0.823 to 1.80 | -- | -- | 14.0 | -- | -- | 1.10 to 20.0 | 0.00937 to 0.900 | -- | | DTUL @ 66 psi (0.45 MPa) (°F) | 120 to 221 | -- | -- | -- | -- | -- | -- | -- | -- | -- | 365 | 158 to 221 | -- | | DTUL @ 264 psi (1.8 MPa) (°F) | 100 to 249 | -- | -- | -- | 127 to 190 | -- | -- | -- | -- | -- | 135 | -- | -- | | CLTE, Flow (in/in/°F) | 0.000040 to 0.00010 | -- | -- | -- | -- | -- | -- | -- | -- | -- | 0.000050 to 0.00010 | 0.000040 to 0.000056 | -- |
SI
|
| Density (g/cm³) | 0.830 to 1.38 | 1.13 | 1.04 to 1.21 | 1.15 to 1.23 | 1.25 to 1.52 | 1.20 to 1.25 | 1.16 to 1.27 | 1.02 to 1.07 | 1.06 to 1.43 | 0.998 to 1.13 | 1.04 to 1.21 | 0.239 to 1.25 | 1.01 to 1.21 | | Melt Mass Flow Rate (g/10 min) | 3.0 to 20 | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | | Flexural Modulus (MPa) | 37.9 to 2690 | -- | -- | -- | 2590 to 3070 | -- | -- | 7.17 to 689 | -- | -- | 558 to 800 | 103 to 2130 | -- | | Tensile Strength (MPa) | 0.0758 to 62.1 | 24.8 to 49.6 | 1.72 to 23.4 | 17.0 to 59.3 | 38.8 to 93.6 | 12.3 to 52.6 | 36.3 to 62.1 | 20.7 to 46.5 | 1.18 to 48.6 | 0.979 to 52.4 | 13.8 to 62.1 | 3.86 to 51.7 | 6.37 to 24.7 | | Tensile Elongation (%) | 2.0 to 54 | 310 to 530 | 75 to 630 | 220 to 890 | 6.8 to 650 | 390 to 700 | 280 to 710 | 180 to 850 | 500 to 750 | 190 to 580 | 180 to 570 | 4.2 to 18 | 130 to 710 | | Rockwell Hardness | 111 | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | | Notched Izod Impact (J/m) | 0.534 to 85.9 | -- | -- | -- | 43.9 to 96.1 | -- | -- | 747 | -- | -- | 58.7 to 1070 | 0.500 to 48.0 | -- | | DTUL @ 66 psi (0.45 MPa) (°C) | 48.9 to 105 | -- | -- | -- | -- | -- | -- | -- | -- | -- | 185 | 70.0 to 105 | -- | | DTUL @ 264 psi (1.8 MPa) (°C) | 38.0 to 121 | -- | -- | -- | 52.8 to 87.8 | -- | -- | -- | -- | -- | 57.2 | -- | -- | | CLTE, Flow (cm/cm/°C) | 0.000072 to 0.00018 | -- | -- | -- | -- | -- | -- | -- | -- | -- | 0.000090 to 0.00018 | 0.000072 to 0.00010 | -- |
|
|