| Polyvinyl Chloride (PVC) Typical Properties |
Share This Page
• Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.46 to 1.52 | 1.15 to 1.29 | 0.360 | 1.07 to 1.32 | 0.360 to 1.40 | 1.14 to 1.45 | 0.778 to 1.47 | 1.29 to 1.58 | 1.14 to 1.45 | 1.18 to 1.33 | 1.16 to 1.26 | 1.68 to 1.70 | | Melt Mass Flow Rate (g/10 min) | 5.0 to 21 | 28 | -- | 3.6 to 30 | -- | 0.42 to 12 | 1.4 to 54 | 19 to 87 | 6.2 to 42 | 0.46 to 42 | -- | -- | | Flexural Modulus (psi) | 334000 to 409000 | 273000 to 352000 | -- | -- | -- | 42000 to 450000 | 306000 to 464000 | 42000 to 278000 | 275000 to 439000 | -- | -- | -- | | Tensile Strength (psi) | 6430 to 9000 | 1220 to 6410 | -- | 230 to 3050 | -- | 17.5 to 4840 | 5450 to 7880 | 2030 to 4540 | 220 to 23800 | 422 to 2580 | 1430 to 2740 | 1800 to 7850 | | Tensile Elongation (%) | 3.5 to 5.5 | 15 to 420 | -- | 300 to 500 | -- | 200 to 450 | 2.6 to 190 | 190 to 300 | 250 to 450 | 350 to 470 | 390 to 600 | 160 to 470 | | Rockwell Hardness | 112 to 117 | 110 | -- | -- | -- | 115 | 89 to 117 | -- | 102 to 119 | -- | -- | -- | | Notched Izod Impact (ft·lb/in) | 0.500 to 7.15 | 0.630 to 14.1 | -- | -- | -- | 2.00 to 37.1 | 0.300 to 20.0 | 0.500 to 1.50 | 0.401 to 22.2 | -- | -- | -- | | DTUL @ 66 psi (0.45 MPa) (°F) | 221 to 230 | 181 to 201 | -- | -- | -- | 117 to 149 | 147 to 174 | 106 to 111 | 201 to 220 | -- | -- | -- | | DTUL @ 264 psi (1.8 MPa) (°F) | 184 to 239 | 161 to 190 | -- | -- | -- | 153 to 182 | 137 to 168 | 97.0 to 97.1 | 142 to 205 | -- | -- | -- | | CLTE, Flow (in/in/°F) | 0.000032 to 0.000040 | 0.000036 to 0.000050 | -- | -- | -- | 0.000033 | 0.000029 to 0.000041 | 0.000041 to 0.000042 | 0.000027 to 0.000049 | -- | -- | -- |
SI
|
| Density (g/cm³) | 1.46 to 1.52 | 1.15 to 1.29 | 0.360 | 1.07 to 1.32 | 0.360 to 1.40 | 1.14 to 1.45 | 0.778 to 1.47 | 1.29 to 1.58 | 1.14 to 1.45 | 1.18 to 1.33 | 1.16 to 1.26 | 1.68 to 1.70 | | Melt Mass Flow Rate (g/10 min) | 5.0 to 21 | 28 | -- | 3.6 to 30 | -- | 0.42 to 12 | 1.4 to 54 | 19 to 87 | 6.2 to 42 | 0.46 to 42 | -- | -- | | Flexural Modulus (MPa) | 2300 to 2820 | 1880 to 2420 | -- | -- | -- | 290 to 3100 | 2110 to 3200 | 290 to 1920 | 1890 to 3030 | -- | -- | -- | | Tensile Strength (MPa) | 44.4 to 62.1 | 8.38 to 44.2 | -- | 1.59 to 21.0 | -- | 0.121 to 33.4 | 37.6 to 54.3 | 14.0 to 31.3 | 1.52 to 164 | 2.91 to 17.8 | 9.83 to 18.9 | 12.4 to 54.1 | | Tensile Elongation (%) | 3.5 to 5.5 | 15 to 420 | -- | 300 to 500 | -- | 200 to 450 | 2.6 to 190 | 190 to 300 | 250 to 450 | 350 to 470 | 390 to 600 | 160 to 470 | | Rockwell Hardness | 112 to 117 | 110 | -- | -- | -- | 115 | 89 to 117 | -- | 102 to 119 | -- | -- | -- | | Notched Izod Impact (J/m) | 26.7 to 382 | 33.6 to 752 | -- | -- | -- | 107 to 1980 | 16.0 to 1070 | 26.7 to 80.1 | 21.4 to 1180 | -- | -- | -- | | DTUL @ 66 psi (0.45 MPa) (°C) | 105 to 110 | 82.8 to 93.9 | -- | -- | -- | 47.0 to 65.0 | 64.0 to 79.1 | 41.1 to 43.9 | 94.1 to 105 | -- | -- | -- | | DTUL @ 264 psi (1.8 MPa) (°C) | 84.5 to 115 | 71.7 to 87.8 | -- | -- | -- | 67.0 to 83.2 | 58.1 to 75.4 | 36.1 to 36.2 | 60.8 to 96.1 | -- | -- | -- | | CLTE, Flow (cm/cm/°C) | 0.000058 to 0.000073 | 0.000064 to 0.000090 | -- | -- | -- | 0.000060 | 0.000052 to 0.000074 | 0.000073 to 0.000075 | 0.000049 to 0.000088 | -- | -- | -- |
|
|