| Phenolic (Phenolic) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 1.41 to 1.51 | 1.33 to 1.62 | | Melt Mass Flow Rate (g/10 min) | -- | -- | | Flexural Modulus (psi) | 943000 to 1.32E+6 | 520000 to 2.80E+6 | | Tensile Strength (psi) | 7220 to 7980 | 5850 to 9270 | | Tensile Elongation (%) | -- | 0.45 to 2.3 | | Rockwell Hardness | -- | 42 to 112 | | Notched Izod Impact (ft·lb/in) | -- | 0.260 to 0.979 | | DTUL at 66 psi (0.45 MPa) (°F) | -- | 392 | | DTUL at 264 psi (1.8 MPa) (°F) | -- | 294 to 574 | | CLTE, Flow (in/in/°F) | -- | 9.5E-6 to 0.000020 |
SI
|
| Specific Gravity (g/cm³) | 1.41 to 1.50 | 1.33 to 1.62 | | Melt Mass Flow Rate (g/10 min) | -- | -- | | Flexural Modulus (MPa) | 6500 to 9110 | 3590 to 19300 | | Tensile Strength (MPa) | 49.7 to 55.0 | 40.4 to 63.9 | | Tensile Elongation (%) | -- | 0.45 to 2.3 | | Rockwell Hardness | -- | 42 to 112 | | Notched Izod Impact (J/m) | -- | 13.9 to 52.3 | | DTUL at 66 psi (0.45 MPa) (°C) | -- | 200 | | DTUL at 264 psi (1.8 MPa) (°C) | -- | 145 to 301 | | CLTE, Flow (cm/cm/°C) | -- | 0.000017 to 0.000036 |
|
|