| Polyarylate (Polyarylate) Typical Properties |
|
Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.20 to 1.36 | | Melt Mass Flow Rate (g/10 min) | -- | | Flexural Modulus (psi) | 305000 to 393000 | | Tensile Strength (psi) | 9140 to 10000 | | Tensile Elongation (%) | 2.5 to 82 | | Rockwell Hardness | 105 to 125 | | Notched Izod Impact (ft·lb/in) | 0.81 to 8.4 | | DTUL @ 66 psi (0.45 MPa) (°F) | 356 | | DTUL @ 264 psi (1.8 MPa) (°F) | 230 to 356 | | CLTE, Flow (in/in/°F) | 0.000034 to 0.000035 |
SI
|
| Density (g/cm³) | 1.20 to 1.36 | | Melt Mass Flow Rate (g/10 min) | -- | | Flexural Modulus (MPa) | 2100 to 2710 | | Tensile Strength (MPa) | 63.0 to 69.0 | | Tensile Elongation (%) | 2.5 to 82 | | Rockwell Hardness | 105 to 125 | | Notched Izod Impact (J/m) | 43 to 450 | | DTUL @ 66 psi (0.45 MPa) (°C) | 180 | | DTUL @ 264 psi (1.8 MPa) (°C) | 110 to 180 | | CLTE, Flow (cm/cm/°C) | 0.000061 to 0.000063 |
|
|