| Polyester (Polyester)
Processing Information |
Share This Page
• Free Access to 80,000 Datasheets
|
|
English
|
| Density (g/cm³) | 1.17 to 1.33 | 1.24 to 1.48 | 1.07 to 1.35 | -- | 1.42 to 1.78 | -- | 1.32 to 1.41 | 1.25 to 1.27 | 1.05 to 1.93 | 1.19 to 1.41 | 1.29 to 1.43 | | Mold Shrinkage, Flow (in/in) | -0.010 to 0.010 | 0.00070 to 0.48 | 0.0055 to 0.012 | -- | 0.0040 to 0.012 | -- | 0.0027 to 0.018 | 0.0035 to 0.0051 | 0.0020 to 0.0034 | 0.0029 to 0.0040 | 0.011 to 0.025 | | Melt Mass Flow Rate (g/10 min) | 2.5 to 22 | 20 to 26 | -- | -- | 5.0 to 43 | -- | -- | 4.0 to 35 | -- | -- | -- | | Drying Temperature (°F) | 154 to 320 | 236 to 269 | 203 to 212 | -- | 250 to 302 | -- | 230 to 356 | 149 to 167 | 230 to 266 | 157 to 176 | 260 | | Drying Time (hr) | 3.0 to 6.1 | 3.0 to 6.1 | 3.5 | -- | 3.0 to 5.0 | -- | 3.9 to 5.6 | 3.0 to 9.0 | 3.0 to 4.0 | 3.0 to 4.1 | 5.0 | | Suggested Max Moisture (%) | 0.020 | 0.020 to 0.052 | -- | -- | 0.020 to 0.040 | -- | 0.0030 to 0.022 | 0.050 | 0.030 to 0.10 | -- | -- | | Suggested Max Regrind (%) | -- | 19 to 26 | -- | -- | -- | -- | -- | -- | -- | -- | -- | | Injection Pressure (psi) | 9000 | 10700 to 13100 | 11400 | -- | 10200 | -- | 14400 to 14500 | 12500 to 14100 | 12500 | -- | 12500 | | Rear Temperature (°F) | 400 to 505 | 438 to 483 | 401 | -- | 480 | -- | 474 to 527 | 401 to 450 | -- | -- | 448 to 485 | | Middle Temperature (°F) | 420 to 515 | 446 to 492 | 446 | -- | 480 to 490 | -- | 484 to 536 | 410 to 473 | -- | -- | 448 to 485 | | Front Temperature (°F) | 435 to 515 | 453 to 513 | 464 | -- | 490 to 500 | -- | 493 to 536 | 424 to 473 | -- | -- | 448 to 485 | | Nozzle Temperature (°F) | 455 to 528 | 463 to 496 | 464 | -- | 505 to 510 | -- | 485 to 536 | 424 to 473 | -- | -- | -- | | Processing (Melt) Temp (°F) | 490 to 545 | 464 to 509 | 464 | -- | 491 to 515 | -- | 493 to 545 | 424 to 500 | 430 to 518 | 490 to 518 | 475 | | Mold Temperature (°F) | 68.0 to 126 | 137 to 197 | 158 | -- | 157 to 176 | -- | 59.0 to 275 | 80.0 to 104 | 175 to 176 | 72.5 to 80.6 | 220 |
SI
|
| Density (g/cm³) | 1.17 to 1.33 | 1.24 to 1.48 | 1.07 to 1.35 | -- | 1.42 to 1.78 | -- | 1.32 to 1.41 | 1.25 to 1.27 | 1.05 to 1.93 | 1.19 to 1.41 | 1.29 to 1.43 | | Mold Shrinkage, Flow (cm/cm) | -0.010 to 0.010 | 0.00070 to 0.48 | 0.0055 to 0.012 | -- | 0.0040 to 0.012 | -- | 0.0027 to 0.018 | 0.0035 to 0.0051 | 0.0020 to 0.0034 | 0.0029 to 0.0040 | 0.011 to 0.025 | | Melt Mass Flow Rate (g/10 min) | 2.5 to 22 | 20 to 26 | -- | -- | 5.0 to 43 | -- | -- | 4.0 to 35 | -- | -- | -- | | Drying Temperature (°C) | 67.9 to 160 | 113 to 132 | 95.0 to 100 | -- | 121 to 150 | -- | 110 to 180 | 65.0 to 75.0 | 110 to 130 | 69.4 to 80.0 | 127 | | Drying Time (hr) | 3.0 to 6.1 | 3.0 to 6.1 | 3.5 | -- | 3.0 to 5.0 | -- | 3.9 to 5.6 | 3.0 to 9.0 | 3.0 to 4.0 | 3.0 to 4.1 | 5.0 | | Suggested Max Moisture (%) | 0.020 | 0.020 to 0.052 | -- | -- | 0.020 to 0.040 | -- | 0.0030 to 0.022 | 0.050 | 0.030 to 0.10 | -- | -- | | Suggested Max Regrind (%) | -- | 19 to 26 | -- | -- | -- | -- | -- | -- | -- | -- | -- | | Injection Pressure (MPa) | 62.1 | 74.0 to 90.0 | 78.4 | -- | 70.0 | -- | 99.3 to 100 | 86.0 to 97.5 | 86.0 | -- | 86.0 to 86.2 | | Rear Temperature (°C) | 204 to 263 | 225 to 250 | 205 | -- | 249 | -- | 246 to 275 | 205 to 232 | -- | -- | 231 to 252 | | Middle Temperature (°C) | 216 to 268 | 230 to 256 | 230 | -- | 249 to 254 | -- | 251 to 280 | 210 to 245 | -- | -- | 231 to 252 | | Front Temperature (°C) | 224 to 268 | 234 to 267 | 240 | -- | 254 to 260 | -- | 256 to 280 | 218 to 245 | -- | -- | 231 to 252 | | Nozzle Temperature (°C) | 235 to 275 | 239 to 258 | 240 | -- | 263 to 266 | -- | 252 to 280 | 218 to 245 | -- | -- | -- | | Processing (Melt) Temp (°C) | 254 to 285 | 240 to 265 | 240 | -- | 255 to 268 | -- | 256 to 285 | 218 to 260 | 221 to 270 | 255 to 270 | 246 | | Mold Temperature (°C) | 20.0 to 52.2 | 58.4 to 91.5 | 70.0 | -- | 69.5 to 80.0 | -- | 15.0 to 135 | 26.7 to 40.1 | 79.5 to 80.0 | 22.5 to 27.0 | 104 to 105 |
|
|