| Polyester (Polyester) Typical Properties |
Share This Page
• Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.17 to 1.33 | 1.24 to 1.48 | 1.07 to 1.35 | -- | 1.42 to 1.78 | -- | 1.32 to 1.41 | 1.25 to 1.27 | 1.05 to 1.93 | 1.19 to 1.41 | 1.29 to 1.43 | | Melt Mass Flow Rate (g/10 min) | 2.5 to 22 | 20 to 26 | -- | -- | 5.0 to 43 | -- | -- | 4.0 to 35 | -- | -- | -- | | Flexural Modulus (psi) | 217000 to 368000 | 202000 to 390000 | 229000 to 472000 | -- | 501000 to 1.77E+6 | -- | 243000 to 497000 | 300000 to 315000 | 535000 to 616000 | 250000 to 325000 | 397000 to 400000 | | Tensile Strength (psi) | 2640 to 8700 | 4690 to 8840 | 5000 to 7160 | -- | 0.00 to 17000 | -- | 3330 to 37400 | 3750 to 7360 | 8190 to 12700 | 6260 to 33700 | 6380 to 8900 | | Tensile Elongation (%) | 3.0 to 17 | 0.57 to 52 | 2.8 to 31 | -- | 0.0 to 5.0 | -- | 2.0 to 160 | 4.0 to 79 | 1.9 to 9.4 | 1.9 to 320 | 9.8 to 10 | | Rockwell Hardness | 103 to 115 | 86 to 120 | 85 to 99 | -- | 80 to 120 | -- | 88 to 120 | 106 to 117 | 103 | 103 to 107 | -- | | Notched Izod Impact (ft·lb/in) | 0.148 to 2.09 | 0.187 to 1.26 | 1.47 to 15.0 | -- | 0.749 to 2.23 | -- | 0.262 to 1.51 | 0.0700 to 26.8 | 0.643 to 1.34 | 0.661 to 6.93 | 0.500 to 0.607 | | DTUL @ 66 psi (0.45 MPa) (°F) | 155 to 166 | 226 to 358 | 212 to 225 | -- | 399 to 426 | -- | 147 to 482 | 153 to 158 | 75.0 to 441 | 163 to 164 | -- | | DTUL @ 264 psi (1.8 MPa) (°F) | 143 to 150 | 112 to 161 | 158 to 212 | -- | 177 to 397 | -- | 136 to 447 | 143 to 147 | 187 to 287 | 141 to 156 | 140 to 151 | | CLTE, Flow (in/in/°F) | 4.0E-6 to 0.00070 | 5.0E-8 to 1.4 | 3.9E-8 to 0.000058 | -- | 9.4E-6 to 0.040 | -- | 9.4E-6 to 0.000086 | 0.000051 | 0.000017 | 9.2E-6 to 0.000010 | -- |
SI
|
| Density (g/cm³) | 1.17 to 1.33 | 1.24 to 1.48 | 1.07 to 1.35 | -- | 1.42 to 1.78 | -- | 1.32 to 1.41 | 1.25 to 1.27 | 1.05 to 1.93 | 1.19 to 1.41 | 1.29 to 1.43 | | Melt Mass Flow Rate (g/10 min) | 2.5 to 22 | 20 to 26 | -- | -- | 5.0 to 43 | -- | -- | 4.0 to 35 | -- | -- | -- | | Flexural Modulus (MPa) | 1500 to 2540 | 1400 to 2690 | 1580 to 3260 | -- | 3450 to 12200 | -- | 1670 to 3430 | 2070 to 2170 | 3690 to 4250 | 1720 to 2240 | 2740 to 2760 | | Tensile Strength (MPa) | 18.2 to 60.0 | 32.4 to 60.9 | 34.5 to 49.4 | -- | 0.00 to 117 | -- | 23.0 to 258 | 25.9 to 50.7 | 56.5 to 87.4 | 43.2 to 232 | 44.0 to 61.4 | | Tensile Elongation (%) | 3.0 to 17 | 0.57 to 52 | 2.8 to 31 | -- | 0.0 to 5.0 | -- | 2.0 to 160 | 4.0 to 79 | 1.9 to 9.4 | 1.9 to 320 | 9.8 to 10 | | Rockwell Hardness | 103 to 115 | 86 to 120 | 85 to 99 | -- | 80 to 120 | -- | 88 to 120 | 106 to 117 | 103 | 103 to 107 | -- | | Notched Izod Impact (J/m) | 7.90 to 111 | 10.0 to 67.5 | 78.5 to 801 | -- | 40.0 to 119 | -- | 14.0 to 80.5 | 3.74 to 1430 | 34.3 to 71.8 | 35.3 to 370 | 26.7 to 32.4 | | DTUL @ 66 psi (0.45 MPa) (°C) | 68.2 to 74.5 | 108 to 181 | 100 to 107 | -- | 204 to 219 | -- | 63.9 to 250 | 67.0 to 70.2 | 23.9 to 227 | 72.7 to 73.4 | -- | | DTUL @ 264 psi (1.8 MPa) (°C) | 61.6 to 65.6 | 44.5 to 71.5 | 70.0 to 100 | -- | 80.3 to 203 | -- | 57.8 to 231 | 61.8 to 64.0 | 86.2 to 142 | 60.6 to 69.0 | 60.0 to 66.0 | | CLTE, Flow (cm/cm/°C) | 7.2E-6 to 0.0013 | 9.0E-8 to 2.4 | 7.0E-8 to 0.00010 | -- | 0.000017 to 0.072 | -- | 0.000017 to 0.00015 | 0.000092 | 0.000030 | 0.000017 to 0.000018 | -- |
|
|