| Polyolefin (Polyolefin) Typical Properties |
Share This Page
• Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.02 | 0.858 to 0.870 | 0.854 to 1.14 | | Melt Mass Flow Rate (g/10 min) | 10 to 36 | 0.40 to 3.6 | 0.040 to 26 | | Flexural Modulus (psi) | 459000 to 464000 | -- | 2030 to 315000 | | Tensile Strength (psi) | 6660 to 9140 | 49.3 to 437 | 72.5 to 21700 | | Tensile Elongation (%) | 1.1 to 3.6 | 600 to 1000 | 2.0 to 510 | | Rockwell Hardness | -- | -- | 20 to 120 | | Notched Izod Impact (ft·lb/in) | 0.468 to 0.478 | -- | 0.131 to 15.3 | | DTUL @ 66 psi (0.45 MPa) (°F) | 167 to 338 | -- | 133 to 226 | | DTUL @ 264 psi (1.8 MPa) (°F) | 140 to 275 | -- | 111 to 255 | | CLTE, Flow (in/in/°F) | -- | -- | 0.000033 to 0.000040 |
SI
|
| Density (g/cm³) | 1.02 | 0.858 to 0.870 | 0.854 to 1.14 | | Melt Mass Flow Rate (g/10 min) | 10 to 36 | 0.40 to 3.6 | 0.040 to 26 | | Flexural Modulus (MPa) | 3170 to 3200 | -- | 14.0 to 2170 | | Tensile Strength (MPa) | 45.9 to 63.0 | 0.340 to 3.01 | 0.500 to 149 | | Tensile Elongation (%) | 1.1 to 3.6 | 600 to 1000 | 2.0 to 510 | | Rockwell Hardness | -- | -- | 20 to 120 | | Notched Izod Impact (J/m) | 25.0 to 25.5 | -- | 7.00 to 818 | | DTUL @ 66 psi (0.45 MPa) (°C) | 75.0 to 170 | -- | 56.3 to 108 | | DTUL @ 264 psi (1.8 MPa) (°C) | 60.0 to 135 | -- | 43.9 to 124 | | CLTE, Flow (cm/cm/°C) | -- | -- | 0.000059 to 0.000072 |
|
|