| Proprietary (Proprietary) Typical Properties |
|
Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 0.900 to 1.14 | | Melt Mass Flow Rate (g/10 min) | 1.5 to 16 | | Flexural Modulus (psi) | 324000 to 331000 | | Tensile Strength (psi) | 3680 to 3770 | | Tensile Elongation (%) | 18 to 110 | | Rockwell Hardness | 72 to 97 | | Notched Izod Impact (ft·lb/in) | 0.40 to 1.0 | | DTUL @ 66 psi (0.45 MPa) (°F) | -- | | DTUL @ 264 psi (1.8 MPa) (°F) | -- | | CLTE, Flow (in/in/°F) | -- |
SI
|
| Density (g/cm³) | 0.900 to 1.14 | | Melt Mass Flow Rate (g/10 min) | 1.5 to 16 | | Flexural Modulus (MPa) | 2240 to 2280 | | Tensile Strength (MPa) | 25.4 to 26.0 | | Tensile Elongation (%) | 18 to 110 | | Rockwell Hardness | 72 to 97 | | Notched Izod Impact (J/m) | 21 to 55 | | DTUL @ 66 psi (0.45 MPa) (°C) | -- | | DTUL @ 264 psi (1.8 MPa) (°C) | -- | | CLTE, Flow (cm/cm/°C) | -- |
|
|