| Styrene Acrylonitrile (SAN) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 1.06 to 1.09 | | Melt Mass Flow Rate (g/10 min) | 0.70 to 26 | | Flexural Modulus (psi) | 364000 to 603000 | | Tensile Strength (psi) | 9240 to 11700 | | Tensile Elongation (%) | 2.0 to 6.3 | | Rockwell Hardness | 74 to 126 | | Notched Izod Impact (ft·lb/in) | 0.184 to 0.507 | | DTUL at 66 psi (0.45 MPa) (°F) | 205 to 220 | | DTUL at 264 psi (1.8 MPa) (°F) | 183 to 219 | | CLTE, Flow (in/in/°F) | 0.000038 to 0.000039 |
SI
|
| Specific Gravity (g/cm³) | 1.06 to 1.08 | | Melt Mass Flow Rate (g/10 min) | 0.70 to 26 | | Flexural Modulus (MPa) | 2510 to 4150 | | Tensile Strength (MPa) | 63.7 to 80.6 | | Tensile Elongation (%) | 2.0 to 6.3 | | Rockwell Hardness | 74 to 126 | | Notched Izod Impact (J/m) | 9.80 to 27.1 | | DTUL at 66 psi (0.45 MPa) (°C) | 96.4 to 104 | | DTUL at 264 psi (1.8 MPa) (°C) | 83.7 to 104 | | CLTE, Flow (cm/cm/°C) | 0.000068 to 0.000070 |
|
|