| Styrene Acrylonitrile Silicone (SAS) Typical Properties |
|
Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.03 to 1.13 | | Melt Mass Flow Rate (g/10 min) | -- | | Flexural Modulus (psi) | 301000 to 365000 | | Tensile Strength (psi) | 5770 to 6560 | | Tensile Elongation (%) | -- | | Rockwell Hardness | -- | | Notched Izod Impact (ft·lb/in) | -- | | DTUL @ 66 psi (0.45 MPa) (°F) | -- | | DTUL @ 264 psi (1.8 MPa) (°F) | 171 to 178 | | CLTE, Flow (in/in/°F) | 0.000039 to 0.000051 |
SI
|
| Density (g/cm³) | 1.03 to 1.13 | | Melt Mass Flow Rate (g/10 min) | -- | | Flexural Modulus (MPa) | 2070 to 2520 | | Tensile Strength (MPa) | 39.8 to 45.2 | | Tensile Elongation (%) | -- | | Rockwell Hardness | -- | | Notched Izod Impact (J/m) | -- | | DTUL @ 66 psi (0.45 MPa) (°C) | -- | | DTUL @ 264 psi (1.8 MPa) (°C) | 77.0 to 81.1 | | CLTE, Flow (cm/cm/°C) | 0.000070 to 0.000091 |
|
|