| Styrene Maleic Anhydride (SMA) Typical Properties |
Share This Page
• Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.06 to 1.17 | | Melt Mass Flow Rate (g/10 min) | 0.40 to 2.9 | | Flexural Modulus (psi) | 294000 to 352000 | | Tensile Strength (psi) | 3500 to 6030 | | Tensile Elongation (%) | 1.3 to 27 | | Rockwell Hardness | 97 to 102 | | Notched Izod Impact (ft·lb/in) | 0.300 to 5.00 | | DTUL @ 66 psi (0.45 MPa) (°F) | 220 to 246 | | DTUL @ 264 psi (1.8 MPa) (°F) | 194 to 214 | | CLTE, Flow (in/in/°F) | 0.000035 to 0.000056 |
SI
|
| Density (g/cm³) | 1.06 to 1.17 | | Melt Mass Flow Rate (g/10 min) | 0.40 to 2.9 | | Flexural Modulus (MPa) | 2030 to 2420 | | Tensile Strength (MPa) | 24.1 to 41.5 | | Tensile Elongation (%) | 1.3 to 27 | | Rockwell Hardness | 97 to 102 | | Notched Izod Impact (J/m) | 16.0 to 267 | | DTUL @ 66 psi (0.45 MPa) (°C) | 105 to 119 | | DTUL @ 264 psi (1.8 MPa) (°C) | 90.0 to 101 | | CLTE, Flow (cm/cm/°C) | 0.000063 to 0.00010 |
|
|