| Silicone (Silicone) Typical Properties |
|
|
|
-
-
-
|
English
|
| Specific Gravity | 0.968 to 1.37 | -- | | Melt Mass Flow Rate (g/10 min) | -- | -- | | Flexural Modulus (psi) | 30000 to 36000 | -- | | Tensile Strength (psi) | 33.0 to 2030 | -- | | Tensile Elongation (%) | 41 to 710 | -- | | Rockwell Hardness | -- | -- | | Notched Izod Impact (ft·lb/in) | -- | -- | | DTUL at 66 psi (0.45 MPa) (°F) | -- | -- | | DTUL at 264 psi (1.8 MPa) (°F) | -- | -- | | CLTE, Flow (in/in/°F) | 0.000069 to 0.00017 | -- |
SI
|
| Specific Gravity (g/cm³) | 0.965 to 1.36 | -- | | Melt Mass Flow Rate (g/10 min) | -- | -- | | Flexural Modulus (MPa) | 207 to 248 | -- | | Tensile Strength (MPa) | 0.228 to 14.0 | -- | | Tensile Elongation (%) | 41 to 710 | -- | | Rockwell Hardness | -- | -- | | Notched Izod Impact (J/m) | -- | -- | | DTUL at 66 psi (0.45 MPa) (°C) | -- | -- | | DTUL at 264 psi (1.8 MPa) (°C) | -- | -- | | CLTE, Flow (cm/cm/°C) | 0.00012 to 0.00030 | -- |
|
|