| Thermoplastic, Unspecified (TP, Unspecified) Typical Properties |
|
Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 0.859 to 1.64 | | Melt Mass Flow Rate (g/10 min) | 0.40 to 22 | | Flexural Modulus (psi) | 2900 to 481000 | | Tensile Strength (psi) | 125 to 11100 | | Tensile Elongation (%) | 0.14 to 30 | | Rockwell Hardness | 34 to 126 | | Notched Izod Impact (ft·lb/in) | 0.020 to 2.3 | | DTUL @ 66 psi (0.45 MPa) (°F) | 118 to 273 | | DTUL @ 264 psi (1.8 MPa) (°F) | 111 to 263 | | CLTE, Flow (in/in/°F) | 6.7E-6 to 0.00011 |
SI
|
| Density (g/cm³) | 0.859 to 1.64 | | Melt Mass Flow Rate (g/10 min) | 0.40 to 22 | | Flexural Modulus (MPa) | 20.0 to 3320 | | Tensile Strength (MPa) | 0.862 to 76.5 | | Tensile Elongation (%) | 0.14 to 30 | | Rockwell Hardness | 34 to 126 | | Notched Izod Impact (J/m) | 1.1 to 120 | | DTUL @ 66 psi (0.45 MPa) (°C) | 47.7 to 134 | | DTUL @ 264 psi (1.8 MPa) (°C) | 44.0 to 128 | | CLTE, Flow (cm/cm/°C) | 0.000012 to 0.00019 |
|
|