|
Thermoplastic Elastomer (TPE) Processing Information
|
|
Free Access to 80,000 Datasheets
|
|
English
|
| Density (g/cm³) | 0.924 to 0.941 | 0.930 to 0.958 | 0.922 to 0.950 | 0.930 to 0.942 | 0.929 to 0.950 | 0.928 to 0.963 | 0.920 to 0.940 | 0.922 to 1.00 | 0.858 to 0.866 | 0.858 to 0.876 | 0.858 to 0.870 | 1.05 to 1.29 | 0.952 to 1.00 | 0.998 to 1.15 | 1.01 to 1.03 | 0.880 to 0.911 | 0.869 to 0.910 | 0.861 to 0.879 | 0.848 to 1.03 | 0.920 to 1.05 | 0.866 to 1.19 | 0.908 to 0.942 | 0.878 to 0.932 | 0.918 to 1.04 | 1.07 to 1.36 | 0.890 to 0.949 | 1.10 to 1.26 | 0.863 to 1.26 | 1.06 to 1.29 | 0.874 to 1.05 | 1.14 to 1.20 | 0.898 to 0.978 | 1.43 | | Mold Shrinkage, Flow (in/in) | -- | -- | -- | -- | -- | -- | -- | -- | 0.0050 to 0.0060 | -- | -- | -- | -- | 0.0035 | 0.0040 to 0.012 | -- | -- | -- | 0.0050 to 0.024 | 0.0040 to 0.014 | 0.014 to 0.024 | -- | 0.011 to 0.014 | 0.013 to 0.017 | 0.012 to 0.018 | 0.015 | 0.0050 to 0.020 | 0.0083 to 0.021 | 0.0035 to 0.021 | 0.000055 to 0.021 | -- | 0.014 to 0.018 | -- | | Melt Mass Flow Rate (g/10 min) | 1.8 to 9.1 | 0.80 to 33 | 0.20 to 8.9 | 0.40 to 10 | 0.30 to 8.5 | 0.70 to 12 | 4.8 to 11 | 0.45 to 23 | 4.0 to 30 | 0.20 to 4.0 | 0.50 to 23 | 10 to 130 | -- | 3.0 to 3.2 | 2.0 to 8.0 | 0.50 to 30 | 0.50 to 3.6 | 2.2 to 80 | 0.20 to 15 | 0.0 to 21 | 0.10 to 23 | 0.10 to 150 | 0.40 to 23 | 1.0 to 25 | -- | 1.0 to 6.2 | 0.50 to 25 | 0.010 to 21 | 0.50 to 27 | 0.090 to 33 | -- | 0.40 to 16 | 5.0 to 12 | | Drying Temperature (°F) | -- | -- | -- | -- | -- | -- | -- | -- | 125 | 158 | -- | -- | -- | -- | 140 to 168 | -- | -- | -- | 125 to 171 | 125 to 126 | 125 to 176 | 158 | -- | 125 to 126 | 200 to 220 | 175 | 175 to 230 | 148 to 177 | 180 to 221 | 150 to 181 | 176 | 158 to 181 | -- | | Drying Time (hr) | -- | -- | -- | -- | -- | -- | -- | -- | 3.0 | 3.0 | -- | -- | -- | -- | 5.0 to 6.0 | -- | -- | -- | 0.98 to 3.0 | 0.0 to 3.0 | 2.0 to 3.0 | 3.0 | -- | 3.0 | 2.5 to 3.0 | 2.0 | 2.5 to 3.5 | 0.0 to 730 | 3.5 to 4.0 | 1.9 to 3.5 | 3.0 | 2.8 to 3.0 | -- | | Suggested Max Moisture (%) | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | 0.10 | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | 0.010 to 0.082 | 0.019 to 0.10 | 0.020 to 0.10 | 0.010 to 0.050 | -- | 0.080 | -- | | Suggested Max Regrind (%) | -- | -- | -- | -- | -- | -- | -- | -- | 20 | -- | -- | -- | -- | -- | 10 to 15 | -- | -- | -- | 20 | 20 to 25 | 20 to 21 | -- | -- | 25 | -- | -- | 25 | 20 to 21 | -- | 20 | -- | 20 | -- | | Injection Pressure (psi) | -- | -- | -- | -- | -- | -- | -- | -- | 750 | -- | -- | -- | -- | -- | 7500 to 9430 | -- | -- | -- | 750 to 782 | 600 to 1200 | 600 to 7740 | -- | 600 | 750 to 12500 | 12500 to 12600 | 500 to 12500 | -- | 325 to 3760 | 12500 | 600 to 15000 | -- | 600 to 15000 | 600 | | Rear Temperature (°F) | -- | -- | -- | -- | -- | -- | -- | -- | 175 | -- | -- | -- | -- | -- | -- | -- | -- | -- | 347 to 356 | 175 to 388 | 349 to 387 | 338 to 356 | 390 | 175 | -- | 348 to 361 | 353 to 448 | 316 to 413 | 356 to 410 | 318 to 423 | 338 to 357 | 288 to 393 | 380 | | Middle Temperature (°F) | -- | -- | -- | -- | -- | -- | -- | -- | 438 | -- | -- | -- | -- | -- | -- | -- | -- | -- | 347 to 392 | 311 to 383 | 352 to 444 | 356 to 374 | -- | 323 | -- | 348 to 371 | 335 to 466 | 352 to 419 | 381 to 428 | 335 to 432 | 356 to 375 | 323 to 395 | 390 | | Front Temperature (°F) | -- | -- | -- | -- | -- | -- | -- | -- | 438 | -- | -- | -- | -- | -- | -- | -- | -- | -- | 347 to 392 | 311 to 384 | 353 to 443 | 365 to 428 | 410 | 368 | -- | 348 to 381 | 390 to 475 | 379 to 431 | 381 to 457 | 353 to 440 | 374 to 393 | 355 to 404 | 400 | | Nozzle Temperature (°F) | -- | -- | -- | -- | -- | -- | -- | -- | 455 | -- | -- | -- | -- | -- | -- | -- | -- | -- | 347 to 348 | 328 to 400 | 352 to 457 | 374 to 464 | 435 | 390 | -- | 390 to 391 | 405 to 474 | 360 to 438 | 383 to 455 | 356 to 428 | 383 to 403 | 361 to 438 | 410 | | Processing (Melt) Temp (°F) | -- | -- | 419 | -- | -- | 454 to 455 | -- | -- | -- | 464 | -- | 330 to 350 | -- | -- | 409 to 504 | -- | -- | -- | 362 to 482 | 311 to 450 | 353 to 483 | -- | -- | 350 to 363 | 393 to 435 | 390 to 391 | 404 to 477 | 390 to 440 | 383 to 456 | 371 to 441 | -- | 355 to 443 | 410 | | Mold Temperature (°F) | -- | -- | 77.0 | -- | -- | -- | -- | -- | 123 | 104 | -- | -- | -- | -- | 68.0 to 109 | -- | -- | -- | 103 to 122 | 72.5 to 113 | 79.9 to 124 | 113 | 115 | 77.5 to 77.6 | 94.9 to 95.0 | 80.0 to 114 | 72.5 to 123 | 74.4 to 123 | 104 to 105 | 76.4 to 115 | 68.0 | 86.7 to 119 | 118 |
SI
|
| Density (g/cm³) | 0.924 to 0.941 | 0.930 to 0.958 | 0.922 to 0.950 | 0.930 to 0.942 | 0.929 to 0.950 | 0.928 to 0.963 | 0.920 to 0.940 | 0.922 to 1.00 | 0.858 to 0.866 | 0.858 to 0.876 | 0.858 to 0.870 | 1.05 to 1.29 | 0.952 to 1.00 | 0.998 to 1.15 | 1.01 to 1.03 | 0.880 to 0.911 | 0.869 to 0.910 | 0.861 to 0.879 | 0.848 to 1.03 | 0.920 to 1.05 | 0.866 to 1.19 | 0.908 to 0.942 | 0.878 to 0.932 | 0.918 to 1.04 | 1.07 to 1.36 | 0.890 to 0.949 | 1.10 to 1.26 | 0.863 to 1.26 | 1.06 to 1.29 | 0.874 to 1.05 | 1.14 to 1.20 | 0.898 to 0.978 | 1.43 | | Mold Shrinkage, Flow (cm/cm) | -- | -- | -- | -- | -- | -- | -- | -- | 0.0050 to 0.0060 | -- | -- | -- | -- | 0.0035 | 0.0040 to 0.012 | -- | -- | -- | 0.0050 to 0.024 | 0.0040 to 0.014 | 0.014 to 0.024 | -- | 0.011 to 0.014 | 0.013 to 0.017 | 0.012 to 0.018 | 0.015 | 0.0050 to 0.020 | 0.0083 to 0.021 | 0.0035 to 0.021 | 0.000055 to 0.021 | -- | 0.014 to 0.018 | -- | | Melt Mass Flow Rate (g/10 min) | 1.8 to 9.1 | 0.80 to 33 | 0.20 to 8.9 | 0.40 to 10 | 0.30 to 8.5 | 0.70 to 12 | 4.8 to 11 | 0.45 to 23 | 4.0 to 30 | 0.20 to 4.0 | 0.50 to 23 | 10 to 130 | -- | 3.0 to 3.2 | 2.0 to 8.0 | 0.50 to 30 | 0.50 to 3.6 | 2.2 to 80 | 0.20 to 15 | 0.0 to 21 | 0.10 to 23 | 0.10 to 150 | 0.40 to 23 | 1.0 to 25 | -- | 1.0 to 6.2 | 0.50 to 25 | 0.010 to 21 | 0.50 to 27 | 0.090 to 33 | -- | 0.40 to 16 | 5.0 to 12 | | Drying Temperature (°C) | -- | -- | -- | -- | -- | -- | -- | -- | 51.7 | 70.0 | -- | -- | -- | -- | 60.0 to 75.6 | -- | -- | -- | 51.7 to 77.2 | 51.7 to 52.4 | 51.7 to 80.0 | 70.0 | -- | 51.7 to 52.3 | 93.3 to 104 | 79.4 | 79.4 to 110 | 64.3 to 80.6 | 82.2 to 105 | 65.3 to 82.5 | 80.0 | 69.8 to 82.7 | -- | | Drying Time (hr) | -- | -- | -- | -- | -- | -- | -- | -- | 3.0 | 3.0 | -- | -- | -- | -- | 5.0 to 6.0 | -- | -- | -- | 0.98 to 3.0 | 0.0 to 3.0 | 2.0 to 3.0 | 3.0 | -- | 3.0 | 2.5 to 3.0 | 2.0 | 2.5 to 3.5 | 0.0 to 730 | 3.5 to 4.0 | 1.9 to 3.5 | 3.0 | 2.8 to 3.0 | -- | | Suggested Max Moisture (%) | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | 0.10 | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | -- | 0.010 to 0.082 | 0.019 to 0.10 | 0.020 to 0.10 | 0.010 to 0.050 | -- | 0.080 | -- | | Suggested Max Regrind (%) | -- | -- | -- | -- | -- | -- | -- | -- | 20 | -- | -- | -- | -- | -- | 10 to 15 | -- | -- | -- | 20 | 20 to 25 | 20 to 21 | -- | -- | 25 | -- | -- | 25 | 20 to 21 | -- | 20 | -- | 20 | -- | | Injection Pressure (MPa) | -- | -- | -- | -- | -- | -- | -- | -- | 5.17 | -- | -- | -- | -- | -- | 51.7 to 65.0 | -- | -- | -- | 5.17 to 5.39 | 4.14 to 8.24 | 4.14 to 53.4 | -- | 4.14 | 5.17 to 86.2 | 86.2 to 86.6 | 3.45 to 86.2 | -- | 2.24 to 25.9 | 86.0 | 4.14 to 104 | -- | 4.14 to 104 | 4.14 | | Rear Temperature (°C) | -- | -- | -- | -- | -- | -- | -- | -- | 79.4 | -- | -- | -- | -- | -- | -- | -- | -- | -- | 175 to 180 | 79.4 to 198 | 176 to 197 | 170 to 180 | 199 | 79.4 | -- | 176 to 183 | 178 to 231 | 158 to 211 | 180 to 210 | 159 to 217 | 170 to 181 | 142 to 201 | 193 | | Middle Temperature (°C) | -- | -- | -- | -- | -- | -- | -- | -- | 225 | -- | -- | -- | -- | -- | -- | -- | -- | -- | 175 to 200 | 155 to 195 | 178 to 229 | 180 to 190 | -- | 161 | -- | 176 to 189 | 168 to 241 | 178 to 215 | 194 to 220 | 168 to 222 | 180 to 191 | 162 to 202 | 199 | | Front Temperature (°C) | -- | -- | -- | -- | -- | -- | -- | -- | 225 | -- | -- | -- | -- | -- | -- | -- | -- | -- | 175 to 200 | 155 to 195 | 178 to 229 | 185 to 220 | 210 | 186 | -- | 176 to 194 | 199 to 246 | 193 to 221 | 194 to 236 | 178 to 227 | 190 to 201 | 179 to 206 | 204 | | Nozzle Temperature (°C) | -- | -- | -- | -- | -- | -- | -- | -- | 235 | -- | -- | -- | -- | -- | -- | -- | -- | -- | 175 to 176 | 164 to 204 | 178 to 236 | 190 to 240 | 224 | 199 | -- | 199 to 200 | 207 to 246 | 182 to 225 | 195 to 235 | 180 to 220 | 195 to 206 | 183 to 226 | 210 | | Processing (Melt) Temp (°C) | -- | -- | 215 | -- | -- | 234 to 235 | -- | -- | -- | 240 | -- | 166 to 177 | -- | -- | 209 to 262 | -- | -- | -- | 184 to 250 | 155 to 232 | 179 to 251 | -- | -- | 177 to 184 | 200 to 224 | 199 to 200 | 207 to 247 | 199 to 227 | 195 to 236 | 189 to 227 | -- | 179 to 228 | 210 | | Mold Temperature (°C) | -- | -- | 25.0 | -- | -- | -- | -- | -- | 50.3 | 40.0 | -- | -- | -- | -- | 20.0 to 43.0 | -- | -- | -- | 39.5 to 50.0 | 22.5 to 45.0 | 26.6 to 51.0 | 45.0 | 46.1 | 25.3 | 35.0 | 26.7 to 45.3 | 22.5 to 50.5 | 23.6 to 50.6 | 39.9 to 40.6 | 24.7 to 46.1 | 20.0 | 30.4 to 48.3 | 47.5 |
|
|