| Thermoplastic Elastomer (TPE) Typical Properties |
Share This Page
• Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 0.924 to 0.941 | 0.930 to 0.958 | 0.922 to 0.950 | 0.928 to 0.944 | 0.929 to 0.950 | 0.928 to 0.963 | 0.920 to 0.940 | 0.922 to 1.00 | 0.858 to 0.866 | 0.858 to 0.876 | 0.858 to 0.870 | 1.06 to 1.27 | 0.952 to 0.980 | 0.998 to 1.15 | 1.01 to 1.09 | 1.01 to 1.02 | 0.880 to 0.921 | 0.869 to 0.910 | 0.861 to 0.879 | 0.848 to 1.03 | 0.920 to 1.05 | 0.866 to 1.19 | 0.908 to 0.942 | 0.878 to 0.914 | 0.918 to 0.938 | 0.917 to 0.956 | 1.10 to 1.29 | 0.859 to 1.23 | 1.06 to 1.29 | 0.874 to 1.00 | 1.14 to 1.20 | 0.917 to 0.979 | | Melt Mass Flow Rate (g/10 min) | 1.8 to 9.1 | 0.80 to 33 | 0.20 to 8.9 | 0.40 to 10 | 0.30 to 8.5 | 0.70 to 12 | 4.8 to 11 | 0.45 to 23 | 4.0 to 30 | 0.20 to 4.0 | 0.50 to 23 | -- | -- | 3.0 to 3.2 | -- | 2.0 to 8.0 | 0.50 to 30 | 0.50 to 8.6 | 2.2 to 80 | 0.20 to 15 | 0.0 to 26 | 0.10 to 23 | 0.10 to 150 | 0.40 to 23 | 2.0 to 41 | 1.0 to 6.2 | 0.50 to 16 | 0.010 to 21 | 4.9 to 27 | 0.10 to 33 | -- | 0.088 to 15 | | Flexural Modulus (psi) | -- | 2900 to 16000 | 17000 to 17400 | 3480 to 18900 | 1160 to 12800 | 4290 to 106000 | 3650 to 9930 | 780 to 1050 | 300000 to 355000 | -- | -- | -- | -- | 390000 to 490000 | -- | 2300 to 54700 | 769 to 12500 | 10200 to 56500 | 1600 to 4130 | 193000 to 341000 | 160000 to 273000 | 15000 to 108000 | -- | -- | -- | 20400 to 26000 | 1020 to 111000 | 270 to 58100 | 2180 to 61200 | 174 to 60200 | -- | 1890 to 101000 | | Tensile Strength (psi) | -- | 725 to 4800 | 218 to 3630 | 375 to 2630 | 845 to 2920 | 1670 to 5400 | 580 to 4260 | 140 to 1890 | 50.0 to 263 | 716 to 2180 | -- | 986 to 1920 | 1440 to 4460 | 9450 to 9500 | 1450 to 5860 | 435 to 7460 | 203 to 10700 | 215 to 6640 | 914 to 2640 | 150 to 5150 | 236 to 4630 | 267 to 2180 | 300 to 2090 | 300 to 17500 | 988 to 4600 | 1350 to 2900 | 284 to 7270 | 44.1 to 7660 | 85.3 to 7330 | 213 to 4080 | 435 to 2340 | 32.0 to 2030 | | Tensile Elongation (%) | -- | 350 to 750 | 13 to 700 | 8.0 to 820 | 360 to 910 | 290 to 660 | 590 to 1100 | 180 to 1100 | 100 to 120 | 260 to 750 | -- | 290 to 470 | 75 to 570 | 3.0 to 4.0 | 8.0 to 500 | 20 to 55 | 6.5 to 650 | 540 to 1000 | 830 to 2000 | 2.0 to 280 | 190 to 1200 | 490 to 770 | 650 to 760 | 100 to 710 | 750 to 1500 | 580 to 600 | 4.0 to 680 | 360 to 810 | 35 to 900 | 3.0 to 840 | 400 to 600 | 20 to 710 | | Rockwell Hardness | -- | -- | -- | -- | -- | -- | -- | -- | 108 to 118 | -- | -- | -- | -- | 60 | -- | -- | -- | -- | -- | 51 to 85 | 18 to 73 | -- | -- | -- | -- | -- | -- | 0 to 85 | -- | 90 to 92 | -- | 45 to 90 | | Notched Izod Impact (ft·lb/in) | -- | -- | -- | -- | -- | 6.80 to 16.0 | -- | -- | 1.74 to 11.4 | -- | -- | -- | -- | 2.50 to 9.00 | -- | 0.950 to 1.90 | -- | -- | -- | 0.370 to 2.44 | 0.337 to 0.789 | 1.32 to 12.2 | -- | -- | -- | 1.20 | 0.375 to 2.54 | 0.749 to 7.00 | 0.551 to 15.0 | 0.525 to 16.8 | -- | 1.09 to 1.36 | | DTUL @ 66 psi (0.45 MPa) (°F) | -- | -- | -- | 88.0 to 91.0 | -- | 93.0 | -- | -- | -- | -- | -- | -- | -- | 156 to 170 | 148 to 230 | 108 to 223 | -- | -- | -- | 171 to 172 | 169 to 193 | 149 to 223 | -- | -- | -- | -- | 108 to 240 | 105 to 279 | 115 to 260 | 126 to 232 | -- | -- | | DTUL @ 264 psi (1.8 MPa) (°F) | -- | -- | -- | -- | -- | -- | -- | -- | 181 to 266 | -- | -- | -- | -- | 151 to 170 | 112 to 131 | 113 | -- | -- | -- | 143 to 185 | 134 to 152 | -- | -- | -- | -- | -- | 104 to 124 | 95.0 to 250 | 77.0 to 297 | 80.0 to 151 | -- | 104 to 195 | | CLTE, Flow (in/in/°F) | -- | -- | -- | -- | -- | 0.000078 to 0.000094 | -- | -- | -- | -- | -- | -- | -- | 0.000037 | 0.000066 to 0.000094 | 0.000078 to 0.00014 | -- | -- | -- | 0.000041 to 0.000042 | -- | -- | -- | -- | -- | -- | 0.000034 to 0.24 | 8.9E-6 to 0.000097 | 0.000061 to 0.00011 | 0.000024 to 0.000056 | -- | -- |
SI
|
| Density (g/cm³) | 0.924 to 0.941 | 0.930 to 0.958 | 0.922 to 0.950 | 0.928 to 0.944 | 0.929 to 0.950 | 0.928 to 0.963 | 0.920 to 0.940 | 0.922 to 1.00 | 0.858 to 0.866 | 0.858 to 0.876 | 0.858 to 0.870 | 1.06 to 1.27 | 0.952 to 0.980 | 0.998 to 1.15 | 1.01 to 1.09 | 1.01 to 1.02 | 0.880 to 0.921 | 0.869 to 0.910 | 0.861 to 0.879 | 0.848 to 1.03 | 0.920 to 1.05 | 0.866 to 1.19 | 0.908 to 0.942 | 0.878 to 0.914 | 0.918 to 0.938 | 0.917 to 0.956 | 1.10 to 1.29 | 0.859 to 1.23 | 1.06 to 1.29 | 0.874 to 1.00 | 1.14 to 1.20 | 0.917 to 0.979 | | Melt Mass Flow Rate (g/10 min) | 1.8 to 9.1 | 0.80 to 33 | 0.20 to 8.9 | 0.40 to 10 | 0.30 to 8.5 | 0.70 to 12 | 4.8 to 11 | 0.45 to 23 | 4.0 to 30 | 0.20 to 4.0 | 0.50 to 23 | -- | -- | 3.0 to 3.2 | -- | 2.0 to 8.0 | 0.50 to 30 | 0.50 to 8.6 | 2.2 to 80 | 0.20 to 15 | 0.0 to 26 | 0.10 to 23 | 0.10 to 150 | 0.40 to 23 | 2.0 to 41 | 1.0 to 6.2 | 0.50 to 16 | 0.010 to 21 | 4.9 to 27 | 0.10 to 33 | -- | 0.088 to 15 | | Flexural Modulus (MPa) | -- | 20.0 to 110 | 117 to 120 | 24.0 to 130 | 8.00 to 88.5 | 29.6 to 731 | 25.2 to 68.5 | 5.38 to 7.24 | 2070 to 2450 | -- | -- | -- | -- | 2690 to 3380 | -- | 15.9 to 377 | 5.30 to 86.3 | 70.0 to 389 | 11.0 to 28.5 | 1330 to 2350 | 1100 to 1880 | 103 to 747 | -- | -- | -- | 140 to 179 | 7.00 to 763 | 1.86 to 401 | 15.0 to 422 | 1.20 to 415 | -- | 13.0 to 695 | | Tensile Strength (MPa) | -- | 5.00 to 33.1 | 1.50 to 25.0 | 2.59 to 18.1 | 5.83 to 20.1 | 11.5 to 37.2 | 4.00 to 29.4 | 0.965 to 13.0 | 0.345 to 1.81 | 4.94 to 15.0 | -- | 6.80 to 13.3 | 9.96 to 30.8 | 65.2 to 65.5 | 10.0 to 40.4 | 3.00 to 51.4 | 1.40 to 74.0 | 1.48 to 45.8 | 6.30 to 18.2 | 1.03 to 35.5 | 1.63 to 31.9 | 1.84 to 15.0 | 2.07 to 14.4 | 2.07 to 121 | 6.81 to 31.7 | 9.32 to 20.0 | 1.96 to 50.1 | 0.304 to 52.8 | 0.588 to 50.5 | 1.47 to 28.1 | 3.00 to 16.1 | 0.221 to 14.0 | | Tensile Elongation (%) | -- | 350 to 750 | 13 to 700 | 8.0 to 820 | 360 to 910 | 290 to 660 | 590 to 1100 | 180 to 1100 | 100 to 120 | 260 to 750 | -- | 290 to 470 | 75 to 570 | 3.0 to 4.0 | 8.0 to 500 | 20 to 55 | 6.5 to 650 | 540 to 1000 | 830 to 2000 | 2.0 to 280 | 190 to 1200 | 490 to 770 | 650 to 760 | 100 to 710 | 750 to 1500 | 580 to 600 | 4.0 to 680 | 360 to 810 | 35 to 900 | 3.0 to 840 | 400 to 600 | 20 to 710 | | Rockwell Hardness | -- | -- | -- | -- | -- | -- | -- | -- | 108 to 118 | -- | -- | -- | -- | 60 | -- | -- | -- | -- | -- | 51 to 85 | 18 to 73 | -- | -- | -- | -- | -- | -- | 0 to 85 | -- | 90 to 92 | -- | 45 to 90 | | Notched Izod Impact (J/m) | -- | -- | -- | -- | -- | 363 to 854 | -- | -- | 93.0 to 608 | -- | -- | -- | -- | 134 to 480 | -- | 50.7 to 101 | -- | -- | -- | 19.8 to 130 | 18.0 to 42.1 | 70.6 to 650 | -- | -- | -- | 64.0 | 20.0 to 136 | 40.0 to 374 | 29.4 to 800 | 28.0 to 897 | -- | 58.2 to 72.7 | | DTUL @ 66 psi (0.45 MPa) (°C) | -- | -- | -- | 31.1 to 32.8 | -- | 33.9 | -- | -- | -- | -- | -- | -- | -- | 68.9 to 76.7 | 64.5 to 110 | 42.0 to 106 | -- | -- | -- | 77.0 to 77.5 | 76.3 to 89.4 | 65.0 to 106 | -- | -- | -- | -- | 42.0 to 116 | 40.6 to 137 | 46.0 to 127 | 52.5 to 111 | -- | -- | | DTUL @ 264 psi (1.8 MPa) (°C) | -- | -- | -- | -- | -- | -- | -- | -- | 82.8 to 130 | -- | -- | -- | -- | 66.1 to 76.7 | 44.5 to 55.0 | 45.0 | -- | -- | -- | 61.6 to 85.0 | 56.8 to 66.7 | -- | -- | -- | -- | -- | 39.9 to 51.3 | 35.0 to 121 | 25.0 to 147 | 26.7 to 66.3 | -- | 40.0 to 90.4 | | CLTE, Flow (cm/cm/°C) | -- | -- | -- | -- | -- | 0.00014 to 0.00017 | -- | -- | -- | -- | -- | -- | -- | 0.000067 | 0.00012 to 0.00017 | 0.00014 to 0.00025 | -- | -- | -- | 0.000075 | -- | -- | -- | -- | -- | -- | 0.000061 to 0.43 | 0.000016 to 0.00018 | 0.00011 to 0.00020 | 0.000043 to 0.00010 | -- | -- |
|
|