| Thermoset (TS) Typical Properties |
|
Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.33 to 1.54 | 1.10 to 2.05 | 1.02 to 1.52 | | Melt Mass Flow Rate (g/10 min) | -- | -- | -- | | Flexural Modulus (psi) | 200000 to 698000 | 30100 to 1.92E+6 | 300000 to 515000 | | Tensile Strength (psi) | 500 to 35800 | 4970 to 11700 | 90.0 to 563 | | Tensile Elongation (%) | 1.0 to 95 | 0.40 to 5.2 | 3.4 to 700 | | Rockwell Hardness | 37 to 95 | 41 to 94 | -- | | Notched Izod Impact (ft·lb/in) | 0.34 to 2.2 | 0.29 to 15 | 0.22 to 3.9 | | DTUL @ 66 psi (0.45 MPa) (°F) | -- | -- | 121 to 134 | | DTUL @ 264 psi (1.8 MPa) (°F) | 464 to 680 | 159 to 504 | 115 to 125 | | CLTE, Flow (in/in/°F) | 0.000015 to 0.000027 | 3.3E-6 to 0.000028 | 2.2E-6 to 0.00010 |
SI
|
| Density (g/cm³) | 1.33 to 1.54 | 1.10 to 2.05 | 1.02 to 1.52 | | Melt Mass Flow Rate (g/10 min) | -- | -- | -- | | Flexural Modulus (MPa) | 1380 to 4810 | 208 to 13200 | 2070 to 3550 | | Tensile Strength (MPa) | 3.45 to 247 | 34.3 to 80.6 | 0.621 to 3.88 | | Tensile Elongation (%) | 1.0 to 95 | 0.40 to 5.2 | 3.4 to 700 | | Rockwell Hardness | 37 to 95 | 41 to 94 | -- | | Notched Izod Impact (J/m) | 18 to 120 | 15 to 810 | 12 to 210 | | DTUL @ 66 psi (0.45 MPa) (°C) | -- | -- | 49.6 to 56.5 | | DTUL @ 264 psi (1.8 MPa) (°C) | 240 to 360 | 70.6 to 262 | 46.2 to 51.5 | | CLTE, Flow (cm/cm/°C) | 0.000026 to 0.000049 | 6.0E-6 to 0.000050 | 4.0E-6 to 0.00018 |
|
|