| Polyurethane Thermoset Elastomer (TSU) Typical Properties |
|
Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 0.991 to 1.23 | | Melt Mass Flow Rate (g/10 min) | -- | | Flexural Modulus (psi) | 3000 to 327000 | | Tensile Strength (psi) | 55.0 to 6020 | | Tensile Elongation (%) | 2.4 to 300 | | Rockwell Hardness | -- | | Notched Izod Impact (ft·lb/in) | 0.26 to 1.3 | | DTUL @ 66 psi (0.45 MPa) (°F) | 124 to 192 | | DTUL @ 264 psi (1.8 MPa) (°F) | 115 to 235 | | CLTE, Flow (in/in/°F) | 0.000058 to 0.000096 |
SI
|
| Density (g/cm³) | 0.991 to 1.23 | | Melt Mass Flow Rate (g/10 min) | -- | | Flexural Modulus (MPa) | 20.7 to 2250 | | Tensile Strength (MPa) | 0.379 to 41.5 | | Tensile Elongation (%) | 2.4 to 300 | | Rockwell Hardness | -- | | Notched Izod Impact (J/m) | 14 to 69 | | DTUL @ 66 psi (0.45 MPa) (°C) | 51.0 to 89.2 | | DTUL @ 264 psi (1.8 MPa) (°C) | 46.0 to 113 | | CLTE, Flow (cm/cm/°C) | 0.00011 to 0.00017 |
|
|