| Vinyl Alcohol (VOH) Typical Properties |
Share This Page
• Free Access to 80,000 Datasheets
|
|
|
-
-
-
|
English
|
| Density (g/cm³) | 1.12 to 1.20 | 1.24 to 1.29 | | Melt Mass Flow Rate (g/10 min) | 0.80 to 12 | 1.0 to 39 | | Flexural Modulus (psi) | 690000 to 696000 | -- | | Tensile Strength (psi) | 3630 to 10800 | 3650 to 6020 | | Tensile Elongation (%) | 1.0 to 20 | 1.7 to 480 | | Rockwell Hardness | 85 to 104 | -- | | Notched Izod Impact (ft·lb/in) | 1.00 to 1.70 | -- | | DTUL @ 66 psi (0.45 MPa) (°F) | -- | -- | | DTUL @ 264 psi (1.8 MPa) (°F) | -- | -- | | CLTE, Flow (in/in/°F) | 0.000060 to 0.00010 | 0.000047 |
SI
|
| Density (g/cm³) | 1.12 to 1.20 | 1.24 to 1.29 | | Melt Mass Flow Rate (g/10 min) | 0.80 to 12 | 1.0 to 39 | | Flexural Modulus (MPa) | 4760 to 4800 | -- | | Tensile Strength (MPa) | 25.0 to 74.4 | 25.2 to 41.5 | | Tensile Elongation (%) | 1.0 to 20 | 1.7 to 480 | | Rockwell Hardness | 85 to 104 | -- | | Notched Izod Impact (J/m) | 53.4 to 90.7 | -- | | DTUL @ 66 psi (0.45 MPa) (°C) | -- | -- | | DTUL @ 264 psi (1.8 MPa) (°C) | -- | -- | | CLTE, Flow (cm/cm/°C) | 0.00011 to 0.00018 | 0.000085 |
|
|