ULTEM* 9085 Resin

Polyether Imide

Supplied by SABIC Innovative Plastics

The technical datasheet with complete property values for ULTEM* 9085 Resin is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution.
General  
Material Status 
  • Commercial: Active
Availability 
  • North America
Features 
  • High Flow
  • Low Smoke Emission
  • Low Toxicity
Agency Ratings 
 
Processing Method 
  • Injection Molding
  • Profile Extrusion
  
Physical
Nominal Value
Unit
Test Method
Specific Gravity      
--
 
 ASTM D792
--
g/cm³
 ISO 1183
Melt Mass-Flow Rate (MFR) (295°C/6.6 kg)
g/10 min
 ASTM D1238
Melt Volume-Flow Rate (MVR) (360°C/5.0 kg)
in³/10min
 ISO 1133
Molding Shrinkage - Flow (0.126 in)
in/in
 Internal Method
Water Absorption     ISO 62
Saturation, 73°F
%
  
Equilibrium, 73°F, 50% RH
%
  
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus      
-- 2
psi
 ASTM D638
--
psi
 ISO 527-2/1
Tensile Strength      
Yield 3
psi
 ASTM D638
Yield
psi
 ISO 527-2/5
Break 3
psi
 ASTM D638
Break
psi
 ISO 527-2/5
Tensile Elongation      
Yield 3
%
 ASTM D638
Yield
%
 ISO 527-2/5
Break 3
%
 ASTM D638
Break
%
 ISO 527-2/5
Flexural Modulus      
1.97 in Span 4
psi
 ASTM D790
-- 5
psi
 ISO 178
Flexural Strength      
-- 5, 6
psi
 ISO 178
Yield, 1.97 in Span 4
psi
 ASTM D790
Impact
Nominal Value
Unit
Test Method
Notched Izod Impact      
73°F
ft·lb/in
 ASTM D256
73°F 7
ft·lb/in²
 ISO 180/1A
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load      
264 psi, Unannealed, 0.126 in
°F
 ASTM D648
264 psi, Unannealed, 2.52 in Span 8
°F
 ISO 75-2/Af
Vicat Softening Temperature
°F
 ISO 306/B120
Flammability
Nominal Value
Unit
Test Method
Oxygen Index
%
 ASTM D2863
FAA Flammability 9
 
 FAR 25.853
OSU Peak Heat Release Rate 10
kW/m²
 FAR 25.853
OSU Total Heat Release 11
kW·min/m²
 FAR 25.853
Vertical Burn Test - Test a (60 s), passes at
sec
 FAR 25.853
Related Terminology
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics, GE Polymerland

Product names can be difficult to match. You may have searched any one of these terms to find this product: ULTEM* 9085 Resin, ULTEM 9085 Resin, ULTEM* , ULTEM, ULTEM9085Resin, 9085 Resin, 9085Resin, Polyether Imide, PEI, SABIC IP, PolyetherImide, Resin9085
Features
Features may also be described by the following terms: High Flow, High Melt, High MFI, Low Smoke Emission, Low Toxicity.
Agency Ratings
This plastic material has 2 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FAR (1), OSU (1).
Injection
Nominal Value
Unit
 
Drying Temperature
°F
  
Drying Time
hr
  
Suggested Max Moisture
%
  
Suggested Shot Size
%
  
Rear Temperature
°F
  
Middle Temperature
°F
  
Front Temperature
°F
  
Nozzle Temperature
°F
  
Processing (Melt) Temp
°F
  
Mold Temperature
°F
  
Back Pressure
psi
  
Screw Speed
rpm
  
Vent Depth
in
  
Extrusion
Nominal Value
Unit
 
Drying Temperature
°F
  
Drying Time
hr
  
Suggested Max Moisture
%
  
Hopper Temperature
°F
  
Cylinder Zone 1 Temp.
°F
  
Cylinder Zone 2 Temp.
°F
  
Cylinder Zone 3 Temp.
°F
  
Cylinder Zone 4 Temp.
°F
  
Adapter Temperature
°F
  
Melt Temperature
°F
  
Die Temperature
°F
  
Calibration Temp, First
°F
  
Calibration Temp, Second
°F
  
Notes
1Typical properties: these are not to be construed as specifications.
20.20 in/min
3Type I, 0.20 in/min
40.051 in/min
50.079 in/min
6Yield
780*10*4
880*10*4 mm
9Method A/B
105 minute test
112 minute test
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.