Vision PPC BL1010 T30 AKG Polymers Polypropylene Homopolymer (Talc Filler, 30%)

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/2.16 kg)		in³/10min	ISO 1133
Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus		psi	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (73°F)		ft·lb/in²	ISO 179
Charpy Unnotched Impact Strength (73°F)			ISO 179
Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)			ISO 868
Additional Information
Melt Volume - Flow Rate (MVR), ISO 1133, 230°C/2.16 kg: 10 to 16 cm³/10min Density, Internal: 1.10 to 1.14 g/cm³ The values listed for Charpy Impact Strength ISO179, were tested in accordance with DIN 53453. Charpy Notched Impact Strength, DIN 53453: >8 kJ/m² Falling Weight Impact Strength, Internal, 23°C: >100 kgcm Flexural Modulus, ISO 178: >1800 MPa Hardness Shore D, Internal: 62 to 66 Non virgin polymer content, Internal: 65% Talc Filler Content: 28 to 32%
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Vision® PPC BL1010 T30, Vision PPC BL1010 T30, Vision® , Vision, VisionPPCBL1010T30, PPC BL 1010 T 30, PPC BL1010 T30, PPCBL, BL1010, 1010T, T30, PPCBL1010T30, Polypropylene Homopolymer, PP Homopolymer, Polypropylene, PP, AKG Polymers, PolypropyleneHomopolymer, PPHomopolymer, BLPPC
Features
Features may also be described by the following terms: High Impact Resistance.
Uses
Uses may also be described by the following terms: Automotive Applications, Automotive Sector.

Notes

¹Typical properties: these are not to be construed as specifications.

Vision® PPC BL1010 T30