Density
|
|
g/cm³
|
ISO 1183 |
|
Apparent Density 2
|
|
g/cm³
|
ISO 60 |
|
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)
|
|
g/10 min
|
ISO 1133 |
|
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)
|
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
|
|
|
|
Across Flow
|
|
%
|
ISO 2577 |
|
Flow
|
|
%
|
ISO 2577 |
|
Across Flow: 0.0787 in 3
|
|
%
|
ISO 294-4 |
|
Flow: 0.0787 in 3
|
|
%
|
ISO 294-4 |
|
Water Absorption
|
|
|
ISO 62 |
|
Saturation, 73°F
|
|
%
|
|
|
Equilibrium, 73°F, 50% RH
|
|
%
|
|
|
Tensile Modulus (73°F)
|
|
psi
|
ISO 527-2/1 |
|
Tensile Stress
|
|
|
ISO 527-2/5 |
|
Yield, 73°F
|
|
psi
|
|
|
Break, 73°F
|
|
psi
|
|
|
Tensile Strain
|
|
|
ISO 527-2/5 |
|
Yield, 73°F
|
|
%
|
|
|
Break, 73°F
|
|
%
|
|
|
Tensile Creep Modulus
|
|
|
ISO 899-1 |
|
1 hr
|
|
psi
|
|
|
1000 hr
|
|
psi
|
|
|
Flexural Modulus 4 (73°F)
|
|
psi
|
ISO 178 |
|
Flexural Strength 4
|
|
|
ISO 178 |
|
3.5% Strain, 73°F
|
|
psi
|
|
|
73°F
|
|
psi
|
|
|
Flexural Strain at Flexural Strength 5 (73°F)
|
|
%
|
ISO 178 |
|
Charpy Notched Impact Strength 6 (73°F, Complete Break)
|
|
ft·lb/in²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength
|
|
|
ISO 179/1eU |
|
-76°F, Complete Break
|
|
ft·lb/in²
|
|
|
-22°F, Complete Break
|
|
ft·lb/in²
|
|
|
73°F, Complete Break
|
|
ft·lb/in²
|
|
|
Notched Izod Impact Strength 7 (73°F, Complete Break)
|
|
ft·lb/in²
|
ISO 180/A |
|
Multi-Axial Instrumented Impact Energy
|
|
|
ISO 6603-2 |
|
-22°F
|
|
ft·lb
|
|
|
73°F
|
|
ft·lb
|
|
|
Multi-Axial Instrumented Impact Peak Force
|
|
|
ISO 6603-2 |
|
-22°F
|
|
lbf
|
|
|
73°F
|
|
lbf
|
|
|
Ball Indentation Hardness
|
|
psi
|
ISO 2039-1 |
|
Heat Deflection Temperature
|
|
|
|
|
66 psi, Unannealed
|
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
°F
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
|
°F
|
ISO 306/B50 |
|
--
|
|
°F
|
ISO 306/B120 |
|
Ball Pressure Test (277°F)
|
|
|
IEC 60695-10-2 |
|
CLTE
|
|
|
ISO 11359-2 |
|
Flow: 73 to 131°F
|
|
in/in/°F
|
|
|
Transverse: 73 to 131°F
|
|
in/in/°F
|
|
|
Thermal Conductivity (73°F)
|
|
Btu·in/hr/ft²/°F
|
ISO 8302 |
|
Surface Resistivity
|
|
ohm
|
IEC 60093 |
|
Volume Resistivity (73°F)
|
|
ohm·cm
|
IEC 60093 |
|
Relative Permittivity
|
|
|
IEC 60250 |
|
73°F, 100 Hz
|
|
|
|
|
73°F, 1 MHz
|
|
|
|
|
Dissipation Factor
|
|
|
IEC 60250 |
|
73°F, 100 Hz
|
|
|
|
|
73°F, 1 MHz
|
|
|
|
|
Comparative Tracking Index
|
|
|
IEC 60112 |
|
Solution A
|
|
V
|
|
|
Solution B
|
|
V
|
|
|
Electric Strength (73°F, 0.0394 in)
|
|
V/mil
|
IEC 60243-1 |
|
Flame Rating - UL
|
|
|
UL 94 |
|
0.0591 in
|
|
|
|
|
0.118 in, NC, BK, GY
|
|
|
|
|
0.236 in
|
|
|
|
|
Glow Wire Flammability Index
|
|
|
IEC 60695-2-12 |
|
0.0295 in
|
|
°F
|
|
|
0.0591 in
|
|
°F
|
|
|
0.118 in
|
|
°F
|
|
|
Glow Wire Ignition Temperature
|
|
|
IEC 60695-2-13 |
|
3.94E-8 in
|
|
°F
|
|
|
5.91E-8 in
|
|
°F
|
|
|
1.18E-7 in
|
|
°F
|
|
|
Oxygen Index 8
|
|
%
|
ISO 4589-2 |
|
Application of Flame from Small Burner 9 (78.7 mil)
|
|
|
DIN 53438-1, -3 |
|
Burning Rate 10 (< 39.4 mil)
|
|
|
ISO 3795 |
|
Flash Ignition Temperature
|
|
°F
|
ASTM D1929 |
|
Self Ingnition Temperature
|
|
°F
|
ASTM D1929 |
|
RTI Str (0.0591 in)
|
|
°F
|
UL 746 |
|
RTI Imp (0.0591 in)
|
|
°F
|
UL 746 |
|
RTI Elec (0.0591 in)
|
|
°F
|
UL 746 |
|
Electrolytical Corrosion
|
|
|
IEC 60426 |
|
This supplier and product may also be known by these terms: Macrolon, Makralon
Product names can be difficult to match. You may have searched any one of these terms to find this product: Makrolon® 9417, Makrolon 9417, Makrolon® , Makrolon, Makrolon9417, 9417, Polycarbonate, PC, Bayer Euro
|
|
Features may also be described by the following terms: High Viscosity, Good Mold Release, Easy Release, Good Demolding, Bromine Free, No Bromine Content, No Chlorine Content, Chlorine Free.
|