NORYL GTX GTX934 Resin SABIC IP Asia Polyphenylene Ether + PS + Nylon

Product Description

NORYL GTX934 is an unfilled GTX grade with improved processability and heat ageing performance.

General

Material Status

Commercial: Active

Availability

Asia Pacific

Features

Good Heat Aging Resistance

Good Processability

Processing Method

Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--			ASTM D792
--		g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (280°C/5.0 kg)		g/10 min	ASTM D1238
Melt Volume-Flow Rate (MVR) (280°C/5.0 kg)		in³/10min	ISO 1133
Molding Shrinkage			Internal Method
Flow ²		in/in
Flow: 0.126 in		in/in
Across Flow: 0.126 in		in/in
Water Absorption			ISO 62
Saturation, 73°F		%
Equilibrium, 73°F, 50% RH		%
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
--³		psi	ASTM D638
--		psi	ISO 527-2/1
Tensile Strength
Yield⁴		psi	ASTM D638
Yield		psi	ISO 527-2/50
Break⁴		psi	ASTM D638
Break		psi	ISO 527-2/50
Tensile Elongation
Yield⁴		%	ASTM D638
Yield		%	ISO 527-2/50
Break⁴		%	ASTM D638
Break		%	ISO 527-2/50
Flexural Modulus
1.97 in Span⁵		psi	ASTM D790
--⁶		psi	ISO 178
Flexural Strength
--^6, 7		psi	ISO 178
Yield, 1.97 in Span⁵		psi	ASTM D790
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength⁸			ISO 179/1eA
-22°F		ft·lb/in²
73°F		ft·lb/in²
Notched Izod Impact
-22°F		ft·lb/in	ASTM D256
73°F		ft·lb/in	ASTM D256
-22°F⁹		ft·lb/in²	ISO 180/1A
73°F⁹		ft·lb/in²	ISO 180/1A
Instrumented Dart Impact (73°F, Total Energy)		in·lb	ASTM D3763
Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness (H 358/30)		psi	ISO 2039-1
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
66 psi, Unannealed, 0.126 in		°F	ASTM D648
66 psi, Unannealed, 3.94 in Span¹⁰		°F	ISO 75-2/Be
Vicat Softening Temperature
--		°F	ASTM D1525¹¹, ISO 306/B120¹¹
--		°F	ISO 306/A50
--		°F	ISO 306/B50
Ball Pressure Test (257°F)			IEC 60695-10-2
CLTE
Flow: -40 to 104°F		in/in/°F	ASTM E831
Flow: 73 to 140°F		in/in/°F	ISO 11359-2
Transverse: -40 to 104°F		in/in/°F	ASTM E831
Transverse: 73 to 140°F		in/in/°F	ISO 11359-2
Thermal Conductivity		Btu·in/hr/ft²/°F	ISO 8302
Related Terminology
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics Product names can be difficult to match. You may have searched any one of these terms to find this product: NORYL GTX* GTX934 Resin, NORYL GTX GTX934 Resin, NORYL GTX* , NORYL GTX, NORYLGTXGTX934Resin, NORYLGTX, GTX 934 Resin, GTX934 Resin, GTX934, 934Resin, GTX934Resin, Polyphenylene Ether + PS + Nylon, Polyphenylene Ether PS Nylon, Polyphenylene Ether : PS : Nylon, Polyphenylene Ether / PS / Nylon, Polyphenylene Ether - PS - Nylon, Polyphenylene Ether _ PS _ Nylon, Polyphenylene Ether PS Nylon, PPE+PS+Nylon, PPEPSNylon, PPE:PS:Nylon, PPE/PS/Nylon, PPE-PS-Nylon, PPE_PS_Nylon, PPE PS Nylon, Polyphenylene Ether, PPE, SABIC IP Asia, PolyphenyleneEtherPSNylon, PolyphenyleneEther, PolyphenyleneEther_PS_Nylon, 934GTX
Features
Features may also be described by the following terms: Good Heat Aging Resistance, Good Processability, Easy Processing.

Injection	Nominal Value	Unit
Drying Temperature		°F
Drying Time		hr
Suggested Max Moisture		%
Hopper Temperature		°F
Rear Temperature		°F
Middle Temperature		°F
Front Temperature		°F
Nozzle Temperature		°F
Processing (Melt) Temp		°F
Mold Temperature		°F
Injection Notes
Minimum Moisture Content: 0.02 %

Notes

¹Typical properties: these are not to be construed as specifications.

²Tensile Bar

³2.0 in/min

⁴Type I, 2.0 in/min

⁵0.051 in/min

⁶0.079 in/min

⁷Yield

⁸80*10*4 sp=62mm

⁹80*10*4

¹⁰120*10*4 mm

¹¹Rate B (120°C/h), Loading 2 (50 N)

NORYL GTX* GTX934 Resin

Polyphenylene Ether + PS + Nylon

Supplied by SABIC Innovative Plastics Asia Pacific