Density
|
|
g/cm³
|
ASTM D1505 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Molding Shrinkage - Flow
|
|
in/in
|
ASTM D955 |
|
Water Absorption (24 hr)
|
|
%
|
ASTM D570 |
|
Environmental Stress-Cracking Resistance (10% Igepal)
|
|
hr
|
ASTM D1693B |
|
Tensile Strength (Yield)
|
|
psi
|
ASTM D638 |
|
Tensile Elongation (Break)
|
|
%
|
ASTM D638 |
|
Flexural Modulus
|
|
psi
|
ASTM D790 |
|
Notched Izod Impact
|
|
ft·lb/in
|
ASTM D256 |
|
Rockwell Hardness (R-Scale)
|
|
|
ASTM D785 |
|
Deflection Temperature Under Load (264 psi, Unannealed)
|
|
°F
|
ASTM D648 |
|
Vicat Softening Temperature
|
|
°F
|
ASTM D1525 |
|
Melting Temperature
|
|
°F
|
DSC |
|
CLTE - Flow
|
|
in/in/°F
|
ASTM D696 |
|
Specific Heat
|
|
Btu/lb/°F
|
ASTM C351 |
|
Volume Resistivity
|
|
ohm·cm
|
ASTM D257 |
|
Dielectric Strength 2
|
|
V/mil
|
ASTM D149 |
|
Dielectric Constant (1.00 GHz)
|
|
|
ASTM D150 |
|
Dissipation Factor (1.00 GHz)
|
|
|
ASTM D150 |
|
The values listed as Mold Shrink ASTM D955 and Specific Heat ASTM C351, were tested in accordance with KPIC method.
Brittleness Temperature, KPIC method: <-70E-4 cal cm/cm sec °C
Water Absorption @ 24 hrs, ASTM D570: <0.01%
Tensile Elongation at Break, ASTM D638: >500%
Notched Izod Impact, ASTM D256: > 50 kg/cm/cm (490 J/m)
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: HIDEN® B302, HIDEN B302, HIDEN® , HIDEN, HIDENB302, B 302, B302, Polyethylene, High Density, Polyethylene High Density, HDPE, Polyethylene, PE, Yuhwa, PolyethyleneHighDensity, 302B
|
|
Features may also be described by the following terms: Good Processability, Easy Processing, Good Surface Finish.
|
|
Uses may also be described by the following terms: Cosmetic Packaging, Food Containers, Food Container.
|
|
This plastic material has 1 certifications from the following agencies (the number in parentheses shows the number of certifications for that agency): FDA (1).
|