Density
|
|
|
g/cm³
|
ISO 1183 |
|
Water Absorption
|
|
|
|
ISO 62 |
|
73°F, 24 hr
|
|
|
%
|
|
|
Saturation, 73°F
|
|
|
%
|
|
|
Tensile Modulus
|
|
|
psi
|
ISO 527-2 |
|
Tensile Stress
|
|
|
|
ISO 527-2 |
|
Yield
|
|
|
psi
|
|
|
Break
|
|
|
psi
|
|
|
Tensile Strain (Break)
|
|
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
|
|
psi
|
ISO 178 |
|
Coefficient of Friction
|
|
|
|
ASTM D1894 |
|
vs. Steel - Dynamic
|
|
|
|
|
|
vs. Steel - Static
|
|
|
|
|
|
Notched Izod Impact Strength
|
|
|
ft·lb/in²
|
ISO 180 |
|
Unnotched Izod Impact Strength
|
|
|
|
ISO 180 |
|
Ball Indentation Hardness
|
|
|
psi
|
ISO 2039-1 |
|
Heat Deflection Temperature
|
|
|
|
|
|
66 psi, Unannealed
|
|
--
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
|
--
|
°F
|
ISO 75-2/A |
|
Melting Temperature (DSC)
|
|
|
°F
|
ISO 3146 |
|
CLTE - Flow (68 to 212°F)
|
|
|
in/in/°F
|
ISO 11359-2 |
|
Specific Heat
|
|
|
Btu/lb/°F
|
ASTM C351 |
|
Thermal Conductivity
|
|
|
Btu·in/hr/ft²/°F
|
ISO 8302 |
|
Surface Resistivity
|
|
|
ohms
|
IEC 60093 |
|
Dielectric Constant
|
|
|
|
IEC 60250 |
|
Dissipation Factor
|
|
|
|
IEC 60250 |
|
Electric Strength
|
|
|
V/mil
|
IEC 60243-1 |
|
|
Creep Rate Stress, DIN 53444, 1% Elongation: >8 N/mm²
Creep Rate Stress, DIN 53444, 2% Elongation: >12 N/mm²
Friction Wear: 0.09 µm/Km
Penetration Resistance, DIN 53482: 1E15 ohm-cm
Creepage/leakage Resistance: KA3c
Thermal Expension: 0.1 %/10°C
Safe Temperature Range, short periods: 170°C
Safe Temperature Range, permanent: -30°C
Water Absorption 24h/23C, ISO 62: 2.5 to 3%
Water Absorption Sat/23C, ISO 62: 7.5 to 9 %
Tensile Strain at Break, ISO 527-1-2: > 40%
Notched Izod Impact, ISO 180: >3 kJ/m²
|
|
|
Creep Rate Stress, DIN 53444, 1% Elongation: >8 N/mm²
Creep Rate Stress, DIN 53444, 2% Elongation: >12 N/mm²
Friction Wear: 0.09 µm/Km
Penetration Resistance, DIN 53482: 1E12 ohm-cm
Creepage/leakage Resistance: KA3b
Thermal Expension: 0.1 %/10°C
Safe Temperature Range, short periods: 170°C
Safe Temperature Range, permanent: 120°C
Water Absorption 24h/23C, ISO 62: 2.5 to 3%
Water Absorption Sat/23C, ISO 62: 7.5 to 9 %
Tensile Strain at Break, ISO 527-1-2: > 40%
Notched Izod Impact, ISO 180: >3 kJ/m²
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: LAMIGAMID® 200, LAMIGAMID 200, LAMIGAMID® , LAMIGAMID, LAMIGAMID200, 200, Polyamide 66, Nylon 66, Polyamide, Nylon, pa66, Schwartz, Polyamide66, Nylon66
|
|
|
Generic Name may also be described by the following terms: PA66.
|
|
|
Product names can be difficult to match. You may have searched any one of these terms to find this product: LAMIGAMID® 200, LAMIGAMID 200, LAMIGAMID® , LAMIGAMID, LAMIGAMID200, 200, Polyamide 66, Nylon 66, Polyamide, Nylon, pa66, Schwartz, Polyamide66, Nylon66
Generic Name may also be described by the following terms: PA66.
|