Urochem 136 Perstorp Urea Formaldehyde (Cellulose Filler)

Product Description

Urea- formaldehyde resins fortified with highly refined cellulose as filler, and further modified with minor amounts of special purpose additives, pigments, cure regulators and lubricants.

The Urochem 136 Moulding Compounds can be supplied in an almost unlimited range of colours from translucent light pastels to black.

Moulded parts are free from odour; UV stable with good moisture resistance.

Hard, glossy and scratch resistant surface.

Excellent chemical resistance. Fats, oils and common organic solvents like alcohol and acetone do not attack moulded parts which are also resistant to surfactants and weak bases. They will withstand attack from weak acids for a shorter duration.

Excellent electrical properties (arc quenching, tracking, flame resistance). Oxygen index of 30% is achieved without the use of external flame retardants. No halogens are present in the composition.

Compliant with the requirements of widely used material specifications for amino compounds:
BS 1322 type UF A10 (*)
DIN 7708 type 131.5 (*)
ISO 2112 type UF A10 (*)
UL certified
(*) included in ISO 14527

Fields of application: Optimized for use primarily in the thermoset injection moulding process.

Particularly well suited for electrical components such as sockets, lamp holders, and domestic circuit breakers.

General

Material Status

Commercial: Active

Availability

Asia Pacific

Europe

North America

Filler / Reinforcement

Cellulose Filler

Additive

Lubricant

Unspecified Additive

Features

Alcohol Resistant

Base Resistant

Good Chemical Resistance

Good Electrical Properties

Halogen Free

High Gloss

High Hardness

Low to No Odor

Lubricated

Moisture Resistant

Oil Resistant

Recyclable Material

Renewable Resource Content

Scratch Resistant

Solvent Resistant

Uses

Electrical Parts

RoHS Compliance

Appearance

Colors Available

Forms

Granules

Processing Method

Injection Molding

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ISO 1183
Molding Shrinkage			ISO 2577
--²		%
--		%
Water Absorption		mg	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)		psi	ISO 527-2
Flexural Strength		psi	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength		ft·lb/in²	ISO 179/1eA
Charpy Unnotched Impact Strength		ft·lb/in²	ISO 179/1eU
Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
264 psi, Unannealed		°F	ISO 75-2/A
1160 psi, Unannealed		°F	ISO 75-2/C
Electrical	Nominal Value	Unit	Test Method
Surface Resistivity		ohms	IEC 60093
Volume Resistivity		ohm·cm	IEC 60093
Dielectric Constant			DIN 53483
Comparative Tracking Index		V	IEC 60112
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL			UL 94
Glow Wire Flammability Index³		°F	IEC 707
Oxygen Index		%	ASTM D2863
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: Urochem 136, Urochem , Urochem136, 136, Urea Formaldehyde, Urea Formald, Urea, Perstorp, UreaFormaldehyde, UreaFormald
Features
Features may also be described by the following terms: High Hardness, Hard, Moisture Resistant, Water Resistant, Low Moisture Absorption, Low Water Absorption, Low Odor, High Gloss, Good Chemical Resistance, Chemical Resistant, Good Electrical Properties, Zero Halogen Content, Halogen Free, Renewable Resources, From Renewable Resources, Renewable Resource Derived, Renewable Raw Materials, Renewable Resource Content, Scratch Resistant, Resists Scratches.

Injection	Nominal Value	Unit
Nozzle Temperature		°F
Mold Temperature		°F
Injection Pressure		psi
Holding Pressure		psi
Back Pressure		psi
Injection Notes
Hydraulic injection pressure: 50 to 170 bar Hydraulic back pressure: 7 to 11 bar Injection speed: 100 to 200 cm³/s Barrel inlet temp: 70 to 85°C

Notes

¹Typical properties: these are not to be construed as specifications.

²Post-shrink

³180 sec

Urochem 136

Urea Formaldehyde

Cellulose Filler

Supplied by Chemiplastica, Inc.