IPC PP 4810H-GF Black Internat Poly Polypropylene, Unspecified (Glass Fiber Reinforcement, 10%)

General
Material Status	Commercial: Active
Availability	North America
Filler / Reinforcement	Glass Fiber Reinforcement, 10% Filler by Weight
Appearance	Black
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Specific Gravity			ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)		g/10 min	ASTM D1238
Molding Shrinkage - Flow		in/in	ASTM D955
Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)		psi	ASTM D638
Tensile Elongation (Yield)		%	ASTM D638
Flexural Modulus		psi	ASTM D790
Impact	Nominal Value	Unit	Test Method
Notched Izod Impact		ft·lb/in	ASTM D256A
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
66 psi, Unannealed		°F
264 psi, Unannealed		°F
Additional Information
Density - Specific Gravity, ASTM D792: 0.97 ± 0.02 g/cm³ Melt Mass-Flow Rate, ASTM D1238, 230°C/2.16 kg: 12.0 to 14.0 g/10 min Tensile Elongation @ Yld, ASTM D638: 10.0 ± 1.0% Filler, FLTM BO 6-2: 10% ±2%
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: IPC PP 4810H-GF Black, IPC PP 4810HGF Black, IPC PP , IPCPP4810HGFBlack, IPCPP, 4810 H, PP 4810 H GF Black, PP 4810 H, PP4810H-GF Black, PP4810HGF Black, PP4810H:GF Black, PP4810H/GF Black, PP4810H+GF Black, PP4810H_GF Black, PP4810H GF Black, PP4810, PP4810H, 4810 H GF Black, PP4810HGFBlack, 4810H-GF Black, 4810HGF Black, 4810H:GF Black, 4810H/GF Black, 4810H+GF Black, 4810H_GF Black, 4810H GF Black, 4810H, HGF, GFBlack, PP4810H_GFBlack, 4810HGFBlack, 4810H_GFBlack, Polypropylene, Unspecified, Polypropylene Unspecified, PP, Unspecified, PP Unspecified, Polypropylene, PP, Internat Poly, PolypropyleneUnspecified, PPUnspecified, H4810, 4810PP
Generic Name
Generic Name may also be described by the following terms: Polypropilene, Polypropelene.

Notes

¹Typical properties: these are not to be construed as specifications.

IPC PP 4810H-GF Black

Polypropylene

Glass Fiber Reinforcement, 10%

Supplied by International Polymers Corporation