LNP* Lubricomp* DFL28

Polycarbonate

Glass Fiber Reinforcement

Supplied by SABIC Innovative Plastics Asia Pacific

The technical datasheet with complete property values for LNP* Lubricomp* DFL28 is available to members of the Prospector Plastics Database.
Register to view full datasheet.
Register to View Full Datasheet
Product Description
LNP* Lubricomp* DFL28 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.

Also known as: LNP* Lubricomp* Compound DFL-4028
Product reorder name: DFL28
General  
Material Status 
  • Commercial: Active
Availability 
  • Asia Pacific
Filler / Reinforcement 
  • Glass Fiber Reinforcement
Additive 
  • PTFE Lubricant
Features 
  • Lubricated
Processing Method 
  • Injection Molding
Physical
Nominal Value
Unit
Test Method
Specific Gravity
      
--
 
 ASTM D792
--
g/cm³
 ISO 1183
Molding Shrinkage
      
Flow: 24 hr
in/in
 ASTM D955
Across Flow: 24 hr
in/in
 ASTM D955
Across Flow: 24 hr
%
 ISO 294-4
Flow: 24 hr
%
 ISO 294-4
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
      
-- 2
psi
 ASTM D638
--
psi
 ISO 527-2/1
Tensile Strength
      
Yield
psi
 ASTM D638
Yield
psi
 ISO 527-2
Break
psi
 ASTM D638
Break
psi
 ISO 527-2
Tensile Elongation
     ASTM D638, ISO 527-2
Yield
%
  
Break
%
  
Flexural Modulus
      
--
psi
 ASTM D790
--
psi
 ISO 178
Flexural Strength
      
--
psi
 ASTM D790
--
psi
 ISO 178
Coefficient of Friction
     ASTM D3702 Modified
vs. Itself - Dynamic
 
  
vs. Itself - Static
 
  
Wear Factor - Washer
10^-10 in^5-min/ft-lb-hr
 ASTM D3702 Modified
Impact
Nominal Value
Unit
Test Method
Notched Izod Impact
      
73°F
ft·lb/in
 ASTM D256
73°F 3
ft·lb/in²
 ISO 180/1A
Unnotched Izod Impact
      
73°F
ft·lb/in
 ASTM D4812
73°F 3
ft·lb/in²
 ISO 180/1U
Instrumented Dart Impact
      
73°F, Energy at Peak Load
in·lb
 ASTM D3763
--
ft·lb
 ISO 6603-2
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load
      
66 psi, Unannealed, 0.126 in
°F
 ASTM D648
66 psi, Unannealed, 2.52 in Span 4
°F
 ISO 75-2/Bf
264 psi, Unannealed, 0.126 in
°F
 ASTM D648
264 psi, Unannealed, 2.52 in Span 4
°F
 ISO 75-2/Af
CLTE
     ASTM E831, ISO 11359-2
Flow: -40 to 104°F
in/in/°F
  
Transverse: -40 to 104°F
in/in/°F
  
Related Terminology
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics

Product names can be difficult to match. You may have searched any one of these terms to find this product: LNP* Lubricomp* DFL28, LNP Lubricomp DFL28, LNP* Lubricomp* , LNP Lubricomp, LNPLubricompDFL28, LNPLubricomp, DFL 28, DFL28, Polycarbonate, PC, SABIC IP Asia, 28DFL
Injection
Nominal Value
Unit
 
Drying Temperature
°F
  
Drying Time
hr
  
Suggested Max Moisture
%
  
Rear Temperature
°F
  
Middle Temperature
°F
  
Front Temperature
°F
  
Processing (Melt) Temp
°F
  
Mold Temperature
°F
  
Back Pressure
psi
  
Screw Speed
rpm
  
Notes
1Typical properties: these are not to be construed as specifications.
22.0 in/min
380*10*4
480*10*4 mm
 
IDES
Copyright © 2012 IDES
The information presented on this datasheet was acquired by IDES from the producer of the material. IDES makes substantial efforts to assure the accuracy of this data. However, IDES assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.