LONGLITE PMC T 385 J70 Chang Chun Phenolic (Mineral Filler; Wood Flour)

Product Description

PMC T 385 J70 is a wood flour- and mineral-reinforced phenolic injection moulding compound with improved heat resistance

General

Material Status

Availability

Filler / Reinforcement

Features

Forms

Processing Method

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--			ASTM D792
--		g/cm³	ISO 1183
Molding Shrinkage		%	ISO 2577
Water Absorption
24 hr		%	ASTM D570
73°F, 24 hr		%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Stress
Yield		psi	ISO 527-2
--		psi	ASTM D638
Flexural Strength		psi	ASTM D790, ISO 178
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (264 psi, Unannealed)		°F	ASTM D648, ISO 75-2/A
Electrical	Nominal Value	Unit	Test Method
Surface Resistivity		ohms	ASTM D257, IEC 60093
Volume Resistivity		ohm·cm	ASTM D257, IEC 60093
Dielectric Strength (0.0787 in)		V/mil	ASTM D149, IEC 60243-1
Flammability	Nominal Value	Unit	Test Method
Flame Rating - UL (0.250 in)			UL 94
Additional Information
Spiral Flow, CCP: 60 to 70 cm Heat Resistance, IEC 60216-P1, 2 hr: 180°C Charpy Impact, JIS K7111: 3.6 kg cm/cm²
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: LONGLITE® PMC T 385 J70, LONGLITE PMC T 385 J70, LONGLITE® PMC , LONGLITE PMC, LONGLITEPMCT385J70, LONGLITEPMC, PMCT 385 J 70, PMCT 385 J70, PMCT385, PMC, T 385 J 70, PMCT385J70, T 385 J70, T385, 385J, J70, T385J70, Phenolic, Chang Chun, 385T, 385PMCT
Features
Features may also be described by the following terms: Good Electrical Properties, High Heat Resistance, Good Chemical Resistance, Chemical Resistant, Good Weather Resistance, Weather Resistant, Good Wear Resistance, Wear Resistant, Good Moldability.

Injection	Nominal Value	Unit
Rear Temperature		°F
Middle Temperature		°F
Front Temperature		°F
Nozzle Temperature		°F
Processing (Melt) Temp		°F
Mold Temperature		°F
Injection Rate
Back Pressure		psi
Screw Speed		rpm
Injection Notes
Injection Time: 5 ± 2 sec Hardening Time: 15 ± 5 sec

Notes

¹Typical properties: these are not to be construed as specifications.

LONGLITE® PMC T 385 J70