NORYL FE8000S Resin SABIC IP Asia Polyphenylene Ether + PS

Product Description

Noryl* FE8000S resin is an unfilled modified polyphenylene ether resin designed for fluid handling applications. This resin is suitable for multiple conversion routes and will be available in custom colors.

General

Material Status

Commercial: Active

Availability

Asia Pacific

Uses

Fluid Handling

Appearance

Colors Available

Processing Method

Injection Molding

Profile Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--			ASTM D792
--		g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (300°C/5.0 kg)		g/10 min	ASTM D1238
Melt Volume-Flow Rate (MVR) (300°C/10.0 kg)		in³/10min	ISO 1133
Molding Shrinkage - Flow (0.126 in)		in/in	Internal Method
Water Absorption			ISO 62
Saturation, 73°F		%
Equilibrium, 73°F, 50% RH		%
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
--²		psi	ASTM D638
--		psi	ISO 527-2/1
Tensile Strength
Yield³		psi	ASTM D638
Yield		psi	ISO 527-2/50
Break³		psi	ASTM D638
Break		psi	ISO 527-2/50
Tensile Elongation
Yield³		%	ASTM D638
Yield		%	ISO 527-2/50
Break³		%	ASTM D638
Break		%	ISO 527-2/50
Flexural Modulus
1.97 in Span⁴		psi	ASTM D790
--⁵		psi	ISO 178
Flexural Strength
--^5, 6		psi	ISO 178
Yield, 1.97 in Span⁴		psi	ASTM D790
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength⁷			ISO 179/1eA
-22°F		ft·lb/in²
73°F		ft·lb/in²
Notched Izod Impact
-22°F		ft·lb/in	ASTM D256
73°F		ft·lb/in	ASTM D256
-22°F⁸		ft·lb/in²	ISO 180/1A
73°F⁸		ft·lb/in²	ISO 180/1A
Instrumented Dart Impact (73°F, Total Energy)		in·lb	ASTM D3763
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
66 psi, Unannealed, 0.126 in		°F	ASTM D648
264 psi, Unannealed, 0.126 in		°F	ASTM D648
264 psi, Unannealed, 2.52 in Span⁹		°F	ISO 75-2/Af
Vicat Softening Temperature
--		°F	ASTM D1525¹⁰
--		°F	ISO 306/B50
--		°F	ISO 306/B120
CLTE			ASTM E831, ISO 11359-2
Flow: -40 to 104°F		in/in/°F
Transverse: -40 to 104°F		in/in/°F
Related Terminology
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics Product names can be difficult to match. You may have searched any one of these terms to find this product: NORYL* FE8000S Resin, NORYL FE8000S Resin, NORYL* , NORYL, NORYLFE8000SResin, FE 8000 S Resin, FE8000S Resin, FE8000, 8000S, SResin, FE8000SResin, Polyphenylene Ether + PS, Polyphenylene Ether PS, Polyphenylene Ether : PS, Polyphenylene Ether / PS, Polyphenylene Ether - PS, Polyphenylene Ether _ PS, Polyphenylene Ether PS, PPE+PS, PPEPS, PPE:PS, PPE/PS, PPE-PS, PPE_PS, PPE PS, Polyphenylene Ether, PPE, SABIC IP Asia, PolyphenyleneEtherPS, PolyphenyleneEther, PolyphenyleneEther_PS, 8000FE
Generic Name
Generic Name may also be described by the following terms: PPO.

Injection	Nominal Value	Unit
Drying Temperature		°F
Drying Time		hr
Hopper Temperature		°F
Rear Temperature		°F
Middle Temperature		°F
Front Temperature		°F
Nozzle Temperature		°F
Processing (Melt) Temp		°F
Mold Temperature		°F
Extrusion	Nominal Value	Unit
Drying Temperature		°F
Drying Time		hr
Hopper Temperature		°F
Cylinder Zone 1 Temp.		°F
Cylinder Zone 2 Temp.		°F
Cylinder Zone 3 Temp.		°F
Cylinder Zone 4 Temp.		°F
Adapter Temperature		°F
Melt Temperature		°F
Die Temperature		°F
Calibration Temp, First		°F

Notes

¹Typical properties: these are not to be construed as specifications.

²0.20 in/min

³Type I, 2.0 in/min

⁴0.051 in/min

⁵0.079 in/min

⁶Yield

⁷80*10*4 sp=62mm

⁸80*10*4

⁹80*10*4 mm

¹⁰Rate B (120°C/h), Loading 2 (50 N)

NORYL* FE8000S Resin

Polyphenylene Ether + PS

Supplied by SABIC Innovative Plastics Asia Pacific