XENOY* IQ4840 Resin SABIC IP Asia Polycarbonate + PBT (Mineral Filler, 10%)

Product Description

Xenoy iQ4840 (PBT+PC) resin is an environmental responsible, sustainable, and low carbon footprint resin. It is a 10% mineral filled resin with high modulus and ductile (HMD) characteristics. Xenoy iQ4840 offers a good balance of impact and ductility, excellent pull strength, good fatigue, provides Class A surface which is paintable, and excellent processibilty. It is currently used in painted automotive doorhandles.

General

Material Status

Commercial: Active

Availability

Asia Pacific

Filler / Reinforcement

Mineral Filler, 10% Filler by Weight

Recycled Content

Features

Ductile

Fatigue Resistant

Good Impact Resistance

Good Processability

Good Strength

Good Surface Finish

Paintable

Renewable Resource Content

Uses

Automotive Applications

Automotive Exterior Parts

Processing Method

Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity
--			ASTM D792
--		g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (250°C/5.0 kg)		g/10 min	ASTM D1238
Melt Volume-Flow Rate (MVR) (265°C/5.0 kg)		in³/10min	ISO 1133
Molding Shrinkage - Flow (0.126 in)		in/in	Internal Method
Water Absorption			ISO 62
Saturation, 73°F		%
Equilibrium, 73°F, 50% RH		%
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
--²		psi	ASTM D638
--		psi	ISO 527-2/1
Tensile Strength
Yield³		psi	ASTM D638
Yield		psi	ISO 527-2/5
Break³		psi	ASTM D638
Break		psi	ISO 527-2/5
Tensile Elongation
Yield³		%	ASTM D638
Yield		%	ISO 527-2/5
Break³		%	ASTM D638
Break		%	ISO 527-2/5
Flexural Modulus
1.97 in Span⁴		psi	ASTM D790
--⁵		psi	ISO 178
Flexural Strength
--^5, 6		psi	ISO 178
Yield, 1.97 in Span⁴		psi	ASTM D790
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength⁷ (73°F)		ft·lb/in²	ISO 179/1eA
Notched Izod Impact
-22°F		ft·lb/in	ASTM D256
73°F		ft·lb/in	ASTM D256
-22°F⁸		ft·lb/in²	ISO 180/1A
73°F⁸		ft·lb/in²	ISO 180/1A
Instrumented Dart Impact (73°F, Total Energy)		in·lb	ASTM D3763
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
264 psi, Unannealed, 0.126 in		°F	ASTM D648
264 psi, Unannealed, 2.52 in Span⁹		°F	ISO 75-2/Af
Vicat Softening Temperature
--		°F	ASTM D1525¹⁰
--		°F	ISO 306/B50, ISO 306/B120
CLTE			ASTM E831, ISO 11359-2
Flow: -40 to 104°F		in/in/°F
Transverse: -40 to 104°F		in/in/°F
Related Terminology
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics Product names can be difficult to match. You may have searched any one of these terms to find this product: XENOY* IQ4840 Resin, XENOY IQ4840 Resin, XENOY* , XENOY, XENOYIQ4840Resin, IQ 4840 Resin, IQ4840 Resin, IQ4840, 4840Resin, IQ4840Resin, Polycarbonate + PBT, Polycarbonate PBT, Polycarbonate : PBT, Polycarbonate / PBT, Polycarbonate - PBT, Polycarbonate _ PBT, Polycarbonate PBT, PC+PBT, PCPBT, PC:PBT, PC/PBT, PC-PBT, PC_PBT, PC PBT, Polycarbonate, PC, SABIC IP Asia, PolycarbonatePBT, Polycarbonate_PBT, 4840IQ
Features
Features may also be described by the following terms: Good Impact Resistance, Good Processability, Easy Processing, Good Strength, Good Surface Finish, Renewable Resources, From Renewable Resources, Renewable Resource Derived, Renewable Raw Materials, Renewable Resource Content.
Uses
Uses may also be described by the following terms: Automotive Applications, Automotive Sector.

Injection	Nominal Value	Unit
Drying Temperature		°F
Drying Time		hr
Drying Time, Maximum		hr
Suggested Max Moisture		%
Suggested Shot Size		%
Rear Temperature		°F
Middle Temperature		°F
Front Temperature		°F
Nozzle Temperature		°F
Processing (Melt) Temp		°F
Mold Temperature		°F
Back Pressure		psi
Screw Speed		rpm
Vent Depth		in

Notes

¹Typical properties: these are not to be construed as specifications.

²0.20 in/min

³Type I, 0.20 in/min

⁴0.051 in/min

⁵0.079 in/min

⁶Yield

⁷80*10*4 sp=62mm

⁸80*10*4

⁹80*10*4 mm

¹⁰Rate B (120°C/h), Loading 2 (50 N)

XENOY* IQ4840 Resin

Polycarbonate + PBT

Mineral Filler, 10%

Supplied by SABIC Innovative Plastics Asia Pacific