QAMAR HB18N SPDC Polyethylene, Linear Low Density

General

Material Status

Availability

Features

Uses

Forms

Processing Method

Physical	Nominal Value	Unit	Test Method
Density		g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)		g/10 min	ASTM D1238
Mechanical	Nominal Value	Unit	Test Method
Tensile Stress			JIS K6760
Yield		psi
Break		psi
Tensile Strain (Break)		%	JIS K6760
Apparent Bending Modulus		psi	ASTM D747
Films	Nominal Value	Unit	Test Method
Film Thickness - Tested		mil
Tensile Modulus			ISO IR 1184
MD: 1.2 mil		psi
TD: 1.2 mil		psi
Tensile Stress			JIS Z1702
MD: Break, 1.2 mil		psi
TD: Break, 1.2 mil		psi
Tensile Elongation			JIS Z1702
MD: Break, 1.2 mil		%
TD: Break, 1.2 mil		%
Dart Drop Impact (1.2 mil)		g	ASTM D1709
Elmendorf Tear Strength			ASTM D1922
MD: 1.2 mil		g
TD: 1.2 mil		g
Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)			ASTM D2240
Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature		°F	ASTM D746
Vicat Softening Temperature		°F	ASTM D1525
Melting Temperature		°F	DSC
Optical	Nominal Value	Unit	Test Method
Haze (1.18 mil)		%	ASTM D1003
Related Terminology
Product names can be difficult to match. You may have searched any one of these terms to find this product: QAMAR HB18N, QAMAR , QAMARHB18N, HB 18 N, HB18N, HB18, 18N, Polyethylene, Linear Low Density, Polyethylene Linear Low Density, LLDPE, Polyethylene, PE, SPDC, PolyethyleneLinearLowDensity, 18HB
Features
Features may also be described by the following terms: High Strength, Additive Free, No Additives.
Uses
Uses may also be described by the following terms: Heavy-duty Bags, Heavy Duty Bags.

Extrusion	Nominal Value	Unit
Melt Temperature		°F
Melt Temperature (Aim)		°F
Extrusion Notes
Blow up Ratio: 2 to 4 Screw Type: LLDPE screw Die Lip Gap: 2.0 to 3.0 mm Air Ring: Single or Dual Slit (Wide die)

Notes

¹Typical properties: these are not to be construed as specifications.